Electronics Forum | Thu Nov 17 13:13:49 EST 2005 | Mike
Hello, Some questions.... Are you running lead free? What alloy? What�s your pot temp at? Temp of the board after preheat? Are you getting any solder in the barrels (
Electronics Forum | Fri Nov 27 15:46:28 EST 2009 | jrr3434
Would i be able to use the cast iron pot from my electrovert with out any problems? I thought the tin would dissolve the iron in the pot? This lead free thing is a headache!
Electronics Forum | Wed Jun 29 17:58:12 EDT 2005 | GS
Hello, in Europe (SN100C sold by Balver Zinn) several solder pots have been filled by this alloy. On the paper I heard talking very well in terms of performance and good price, but not data are available ( as I know) about performance and if r
Electronics Forum | Mon Jun 12 07:52:21 EDT 2017 | tch
We have had this issue on our Delta 3 waves and determined that there are small pin holes in the solder pot. We had plates welded to the outside of our solder pot on the lead free wave and this bought us enough time until we could replace the wave, a
Electronics Forum | Sun Nov 27 05:04:02 EST 2016 | pmcg
Never used stainless pots as when we converted to lead free we changed all the pots to titanium. Been using SN100C for many years now, very good results, also use it in reel form in our selective solder machines with great results. Bear in mind the
Electronics Forum | Wed Dec 19 09:41:14 EST 2012 | dyoungquist
What is your solder pot temperature? We found that on a 0.093" multilayer board increasing the temp of the lead free solder from 300C to 315C helped with the barrel fill.
Electronics Forum | Fri Apr 05 18:22:18 EDT 2013 | Adam
We have two ZipaTec 460s Selective Solder Machines, one for Lead and one for Lead-Free. This morning we noticed the solder pot was covered in solder balls, and after asking the operator what they had run, the answer was "Nothing." The operator had al
Electronics Forum | Thu Jul 14 03:01:37 EDT 2005 | fctassembly
Chris, The Asahi SCS7 is Asahi's attempt at copying the SN100C and is a tin/copper/silicon alloy that melts at 227C so no, it is not a low temperature lead free alloy.
Electronics Forum | Fri Nov 18 10:03:32 EST 2005 | dougeidle
Speedline ELECTROVERT sells a Quick Change Pot option and accessories. The option is available as a field Upgrade. Our web page has a dedicated PB Free process section; http://www.speedlinetech.com/lead_free/index.aspx I work for Speedline. I am t
Electronics Forum | Wed Nov 16 09:46:41 EST 2005 | barryg
Has anyone dealt with a dual wave solder system. We are a bit tight in floor space and have to maintain a leaded line , but also need to convert to lead free. We are looking at dual wave systems were you have two pots to wheel into place to run one o