What you are most likely dealing with: Insufficient Pure Sn layer ( multiple causes ) Because elevated temperatures accelerate the diffusion process, the thickness of the Pure Sn layer will reduce during every thermal cycle... ( bakeing PCBs, S
Electronics Forum | Thu Mar 06 11:36:37 EST 2003 | O' Connor
Hi, I'm experiencing a problem on a standard part made many times before -Ni/Au finish PCB, Reflow 100% SMD parts. After reflow the gold on the pads does not fully fuse with the solder paste it remains intact on the extremities of the pads, it seems
Electronics Forum | Mon Apr 06 11:58:42 EDT 2009 | c111
Jeong Ju-young You touched them all up with an iron? Wow! We have also had similar issues. What I did to prove there was a board problem was paste one & reflow one bare board with the same chem (noclean) we saw the non-wetting condition. Then applied
Electronics Forum | Mon Mar 30 11:39:46 EDT 2009 | rgduval
Is this a sample board that you ran without components? If so, I'd get it back to your board house, and ask them to explain to you what's happening. We never did get to a satisfactory root cause on our issue (at least, satisfactory to me). It seem
Electronics Forum | Fri Mar 07 10:51:58 EST 2003 | MA/NY DDave
Hi O'Conner, I hope you also tell us what Universal-GeorgeW discusses with you. It is a little strange seeing his name on this list and his phone number. Gee I can give you his email address but won't.. Again distance engineering is tough. I woul
Electronics Forum | Mon Jan 26 13:13:07 EST 2009 | rgduval
We've had this same problem with the solder wicking to the component terminations. However, in our case, we did not see the pads turning a silver-white color...rather, they exhibited a tarnishing/darkening of the gold. We determined that we had som
Electronics Forum | Wed Sep 10 14:56:57 EDT 2008 | rarnold
I am dealing with a similar uncoalesced solder issue. This defect has come and gone several times during the last 6 months. See image. In my case, I am using conventional SnPb solder and an entire strip of my OSP finished board (includes various de
Electronics Forum | Mon Apr 09 09:39:40 EDT 2018 | justconmac
Having an issue with tracking for the Vitronics Soltec Delta 3. Wave will not give error on "expected PCB at exit" but will still show 1+ pcb's in the wave when the machine is empty. This is causing solder pump to idle unnecessarily. Outfeed sensor i
Electronics Forum | Sat Sep 06 03:48:29 EDT 2008 | rameshr
hai, we r using type 4 solder paste in our pcb assembly process - we are now facing the following problem. 1. two component pads soldering was seemed uncoalesced soldered joint except all the other components. 2. what will be the problem & solution f
Electronics Forum | Mon Sep 08 01:45:35 EDT 2008 | rameshr
1.The Temperature on the pad is 247.C & also it is an lead free profile, the same profile we have used till last lot but we had obsereved this problem earlier to this current batch. 2. Both in Type3 & Type 4 paste we are using because of we are using
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830