Electronics Forum | Mon Jun 08 14:52:16 EDT 1998 | Gary Simbulan
| Earl, et al, | Boy things get old and cold around here fast. I promised more detail on my capactior problem and I thought I could drop something completely different in the same message and tell a tale of solder balls. | First the caps. We stil
Electronics Forum | Tue Jun 09 07:35:23 EDT 1998 | Steve Gregory
Hi there Gary, Your solder ball problem is very similar the problem I experienced, but I was using a water soluble paste at the time. It started by inspectors telling me that they were seeing cold solder on some SIMM's that we had built regularly. W
Electronics Forum | Tue Jun 16 15:01:58 EDT 1998 | Gary Simbulan
There are some common reason for capacitor cracking on my web page if you want to have a look. The document can be downloaded for your reference. | Earl, et al, | Boy things get old and cold around here fast. I promised more detail on my capactior
Electronics Forum | Tue Jun 16 15:00:12 EDT 1998 | Gary Simbulan
There are some common reason for capacitor cracking on my web page if you want to have a look. The document can be downloaded for your reference. | Earl, et al, | Boy things get old and cold around here fast. I promised more detail on my capactior
Electronics Forum | Mon Jun 08 15:29:17 EDT 1998 | Gary Simbulan
| Earl, et al, | Boy things get old and cold around here fast. I promised more detail on my capactior problem and I thought I could drop something completely different in the same message and tell a tale of solder balls. | First the caps. We stil
Electronics Forum | Mon Nov 09 09:44:22 EST 2015 | davef
Purpose. This describes setting-up a wave soldering system set-up for a new assembly design or checking a wave solder machine operation with a test board. Applicability. To be used for new design printed circuit assembles and during machine accept
Electronics Forum | Mon Apr 26 09:46:05 EDT 1999 | C.K.
Chrys: I have checked all the basic elements of Wave solder joint formation: fluxing, preheating, and lastly soldering. For checking the fluxer, i used a product from ECD that's very similar to what you desribed called the flux-o-meter. It did a
Electronics Forum | Thu Aug 01 13:04:57 EDT 2002 | gdstanton
Its interesting. It appears I'm getting conflicting feeback from Indium. This says its not a problem... http://indium.custhelp.com/cgi-bin/indium.cfg/php/enduser/std_adp.php?p_sid=kTDKGClg&p_lva=&p_faqid=355&p_created=1014734692&p_sp=cF9ncmlkc29
Electronics Forum | Mon Apr 19 20:49:13 EDT 1999 | Dave F
| Netters, | | When I reflow a PCB there is a discoloration of silkscreen and mask. It appears if Profile is too hot! But I dont think so, maybe I'm wrong? | | 1. Kester 293 no clean | 2. 2.1 C/s for 30s to 150 C | 3. .5 - .7 C/s for 60s to 185
Electronics Forum | Thu Mar 05 11:53:09 EST 2009 | dcell_1t
Hello to all. for certain time, we have been struggling with some issues on a PCB where have tombstoning on 0402 components (due to pad design) and dewetting in qfp256 0.5 mil pitch (discussed on another threads on this forum) component, we have pro