Electronics Forum | Thu Sep 11 16:50:18 EDT 2003 | davef
Sure it's conceivable that thin HASL can cause tombstoning. Harkening back to the ample discussion in the fine SMTnet Archives, tombstoning is caused by an imbalance in solder surface tension between the two pads of SMT component. The source of thi
Electronics Forum | Thu May 30 10:31:03 EDT 2002 | robbied
Hi Yannick. This is an issue that we are just recently getting into but here is some ifo that I have gathered so far. I have seen/ used 2 different rework machines. The one we have bought is a 'PACE TF2000' which was at the lower cost end of the mar
Electronics Forum | Wed Mar 12 23:00:10 EDT 2008 | davef
You can say: The pad was lifted after reflow and prior to the dye and pry failure analysis. When we see lifted pads, we think: * That's a good solder connection * Either it took a lot of force to lift that pad or the fabrication of the board in the
Electronics Forum | Mon Oct 15 10:51:49 EDT 2001 | davef
On over printing, the general issues are: * Paste deposits being so large that when reflowing, collapse onto many, rather than a single solder mass. * Paste expanding during heating and being close to other solder deposits and bridging [as you say].
Electronics Forum | Tue Feb 19 09:41:26 EST 2008 | slthomas
ECD sells the MOLE, and they sell both the Oven Rider and the Wave Rider to accompany it. The thing is, you can profile both an oven and a wave machine without either if you're willing to just solder your thermocouples to a board. The nice thing ab
Electronics Forum | Wed Mar 02 18:46:02 EST 2005 | Austinj
The tendancy always has been "when in doubt, touch it up"... this is not the way to "verify the process" and is not the best strategy for multiple reasons (unessecary rework, additional labor costs, as well as making the solder joint more brittle, [i
Electronics Forum | Thu Feb 07 14:58:08 EST 2008 | operator
We don't have one of those cool air compressed syringes to dispense adhesive. We have to do it by hand. My question is does anyone have any suggestions on syringe size, needle size etc... for successful deposition of SMT adhesive? I know you can go s
Electronics Forum | Mon Aug 18 15:03:38 EDT 2008 | awegener
I'd like to get more information about pick and place nozzles. How can I learn more? ... What do the nozzles look like? Are there different shapes? Are custom nozzles sometimes used for custom parts or are the nozzles mostly standardized? What kind
Electronics Forum | Wed Aug 21 17:44:32 EDT 2002 | davef
Splitting hairs, I expect SIR of all solderability protection, including OSP, to decrease after reflow. What�s more, I expect the SIR of all solderability protection to pretty much decrease over time. The �comb pattern� test specimens meet requirem
Electronics Forum | Thu May 24 09:11:12 EDT 2001 | Grant Petty
Hi, I would agree. We purchased a TP9 just the slow machine, but we were a small company at the time, and it worked fantastic. Almost no maintenance, and it's a dream to changeover. The serivce in Australia is also very good, but that does not appl