Electronics Forum | Mon Feb 26 14:15:21 EST 2001 | marting
Steve, Currently we are using selective pallets and the best piece of advice is to find a supplier that will be able to handle the requirements of the selective wave process, for example proximity of chips to PIH devices, and pallet thickness etc. We
Electronics Forum | Mon Jan 07 17:51:34 EST 2008 | jmelson
The clear plastic packaging for LEDs is a LOT softer thermoplastic than the thermoset epoxies used on ordinary chips. I think people have had high failure rates when reflowing LEDs in all-plastic packages even at SnPb temperatures, and much worse at
Electronics Forum | Fri Apr 24 20:33:06 EDT 1998 | D.Lange
| Looking for anyone who has experience with high temperature soldering. Need to determine why solder joints are failing. Thermocycling of unit is -40C to +140C, 30 minute dwell time, 10 sec. transition time | Your help is appreciated | Ed Holton |
Electronics Forum | Thu Oct 01 13:31:09 EDT 1998 | FRANK
Assuming that you do not have a solderability problem with the board or part it sounds like you are not pumping the solder up high enough to contact the board plus push into the board by about 1.8mm. Are you using a chip wave in front of the normal
Electronics Forum | Mon Jul 30 21:29:34 EDT 2001 | kennyhktan
Hello Michael & All, Thanks for the feedback. Months ago we receive a number of reject concerning one of the 0805 & 0603 chip capacitor mising (with joint remain on pad)and seriously solder joint fracture. From there I had do some investigation
Electronics Forum | Wed Jun 11 10:27:33 EDT 2003 | caldon
Frank-In addition (Dave gave some good scoop) we use a Pyrex Glass board to run through the wave. This is useful as you can see through the board .....you can watch the flux coverage, preheat, and Wave (be it Chip, lamda, or??) as it goes through the
Electronics Forum | Wed Jun 18 19:26:39 EDT 2003 | gregoryyork
Rules of thumb :- 1. Never over flux - not necessary and waste's money. Never top flux neither 2. Top Board temp. around 70C - 105C or there about's pending what laminate you use. Obviously the more flux you apply the higher heat required/denser PC
Electronics Forum | Fri Jul 24 16:03:56 EDT 1998 | Boris Akselrud
Dave, Thanks for your responce. I think I can manage to solder components by hand. But I am trying to find out an alternative way to solder them. The distance between leads becomes very small and if solder gets in between them I will have hard times
Electronics Forum | Mon Aug 24 21:16:57 EDT 2020 | smith88
I am trying to teach a class and the question came up about loss of metalization of the Earth pad on a chip filter. This pad is on the side of the component. I can not find a IPC call out for this type of side termination other than 3 or 5 sided 9.1.
Electronics Forum | Sun Jun 14 03:58:40 EDT 1998 | Arul vanan
Does any one wave solder the 0402 Chips on the bottom side of a board? Any comments?