Electronics Forum | Tue Feb 16 16:28:30 EST 1999 | Tuffty
| | Can anyone help me with the pros and cons of trying to wave | | solder tantalum and large (1812) ceramic capacitors. I do | | know that one may see fractures on larger cermaic caps, but have not seen much on the tantalums. Any insight as to what
Electronics Forum | Wed Jul 09 19:05:06 EDT 2003 | randywomack
LOZ. Under-cured or out-of-spec(sloppily) applied resist is realistic. What other physics: Shiny resist surface is more prone to balls then matte finish. How about an operator eating fish & chips before handling the boards. Don't laugh... ... saw th
Electronics Forum | Thu Jul 03 18:14:03 EDT 2003 | russ
Kris, I don't know what I HAVEN'T SEEN yet cuz I haven't seen it. (HAHAHA) It is kind of like when you are looking for something and you always say after you found it that it was the last place you looked (Why would anyone keep looking for something
Electronics Forum | Thu Jul 03 07:53:57 EDT 2003 | davef
That has to be the worst of all worlds. Someone goes out and buys the cheapest parts they can find, gives them to you [Loz], and wants you to assemble a perfect product. Well, it would be nice if you could console yourself by making Derick Jetter m
Electronics Forum | Fri Sep 03 14:37:45 EDT 1999 | JohnW
| | We've noticed that there are many different recommendations for pad sizes for various SMT parts. This seems to vary wildly from manufacturer to manufacturer for the same case sizes. Is there any standards that can used used to specify these siz
Electronics Forum | Mon Sep 06 19:59:59 EDT 1999 | armin
| | | We've noticed that there are many different recommendations for pad sizes for various SMT parts. This seems to vary wildly from manufacturer to manufacturer for the same case sizes. Is there any standards that can used used to specify these s
Electronics Forum | Wed Jul 27 15:54:44 EDT 2005 | Hiram
Hi everybody, We have wave solder fixtures made of Durapol and multiple wave solder machines. Most likely we�ll use the same pallets for either tin-lead or lead-free solder for a while (of course after washing the pallets). Should we test the palle
Electronics Forum | Mon Dec 16 16:35:55 EST 2002 | Jim Ferris
Randy, Steve & all, Can you guys point me in the right direction when it come to using selective wave soldering...I am trying to get in-depth information on the Pro's & Con's of having our supplier use this process for our PWA's. (I can see there ar
Electronics Forum | Wed Jul 27 16:27:57 EDT 2005 | GS
It may be you should look for higher TG of Durapol Rgds GS
Electronics Forum | Wed Aug 27 08:00:33 EDT 2008 | cgray
We are using Multicore (MFR 301) from Henkel.