Electronics Forum | Wed Aug 23 08:08:25 EDT 2006 | aj
There are a few variables that you have to consider : 1. Hours available on Wave Machine ( are other products going thru the same wave) 2. What beat rate are the boards being supplied from previous station?i.e. do you envisage the waveto be a bottl
Electronics Forum | Mon Mar 02 23:48:22 EST 2015 | vb7007
Hi We are using Universal carrier for a 2 sided PCB, where the bottom side goes for hand solder the switches after wave. Our issue is, we are getting micro solder balls all over PCB bottom after wave, whereas we got numerous vias, which also turns
Electronics Forum | Wed Jul 17 11:43:31 EDT 2002 | johnw
It depend's as Russ say's on your pallets, things like : material type wall thickness floor thickness selective or open app. but also on the process, the volumes, the number of carriers you have vs the build numbers & cycle time and the machine your
Electronics Forum | Tue Feb 08 06:28:04 EST 2005 | teilo
We manufacture retrofit kits completley out of titanium for all types of Wave Solder Machines, we also manufacture titanium fingers. Avoid solder overflow damage with titanium board stiffners. Also we manufacture board carriers. We have already supp
Electronics Forum | Fri Sep 17 06:01:12 EDT 1999 | Earl Moon
| | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However, a re
Electronics Forum | Tue Feb 23 14:21:17 EST 1999 | Mike McMonagle
| A rash of new products here at my company have designs with multi-pin connectors 90 out-of-phase (orientation)wiht respect to wave direction, which has lead to massive bridging (shorts) problems.... | | Does anyone still use the 45 Degree Pallet
Electronics Forum | Fri May 14 14:52:56 EDT 1999 | Ryan Jennens
| | | | I am looking for anyone who has converted over to VOC Free flux. I need some info on any problems, etc. that you might have had. | | | | | | | | Please E-mail me at wes.ruggles@vickers-systems.com or call at (513) 494-5229 | | | | | | | | T
Electronics Forum | Wed Mar 22 10:29:15 EST 2000 | C.K.
Larry: I've got extensive experience with solder skips on both 0603 and SOT23 devices. We also installed an "Omega" vibrating wave on our machine, but it didn't really have an impact on solder skips. The major difference that the omega makes is in
Electronics Forum | Fri Sep 17 09:54:40 EDT 1999 | Brian
| | | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However, a
Electronics Forum | Fri Sep 17 10:09:17 EDT 1999 | Earl Moon
| | | | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However,