Electronics Forum: (4) (Page 85 of 632)

Re: SRT Rework Station, Model FPD-W

Electronics Forum | Fri Feb 18 05:49:37 EST 2000 | Dean

Can I get an "amen brother"! I'm not familiar with that unit (its not even on their website) but have nothing but positive things to say about SRT! My 1.4 cents (2 cents minus taxes) Dean

Re: Front camera needed

Electronics Forum | Mon Feb 14 16:53:43 EST 2000 | Carol Aviles

Mr. Salam, By contacting Philips at 1-800-4Philips (1-800-474-4547) our technical support group will provide you with free technical support regarding your Emerald and camera requirements. Regards, Carol Aviles

Re: SMT Programming - Parts Database set-up for contract manufacturer

Electronics Forum | Fri Feb 11 12:21:44 EST 2000 | Finepitch Services

Doug, What I've done in past was calling them as 1206T.5, 1206T1.0, SOIC16, RESNET16, SOIC16T5.0, ALCAP4, ALCAP5 etc. T means thickness but for the ALCAP case 4 means 4mm diameter. If you have the time and patience, having a board and attaching a s

PCB laminate dielectric absorption

Electronics Forum | Wed Dec 13 13:42:57 EST 2000 | Mike Ihm

The dielectic absorption characteristic of printed circuit board materials is usually not listed on the manufacturers spec. sheets. Can anyone point me in a direction to help determine which laminate materials might exhibit better dielectric absorpt

Re: Misalignment Issue (CAD Vs. Machine Variables

Electronics Forum | Tue Nov 14 14:19:01 EST 2000 | Claude_Couture

Hi George! Is your CAD in inches and your equipment metric by any chance? If so, make sure your CAD data is converted to metric using at least 4 digit after the decimal (0.1234" for example)

Re: PCB delamination

Electronics Forum | Mon Feb 05 09:21:22 EST 2001 | pteerink

Talking about delamination...... I have a customer requesting info about the max temperature ratings for FR4. Can anyone point me to a good source? ( and yes, I HAVE checked the archives, to no avail.....) Phil

COB module design / layout

Electronics Forum | Thu Oct 26 14:41:33 EDT 2000 | Derek Vanditmars

We are planning on replacing a SMT 100Pin QFP with a COB module that will have two dies that are functionaly equivalent to the old part that will not be available. Questions: 1)Suggestions on substrate material FR-4 or something better? 2)Are there d

Re: COMPONENT LIBRARY

Electronics Forum | Fri Nov 17 11:05:15 EST 2000 | Mika Johnsson

There is such a web based library that includes data that you describe. It has currently about 4 million parts and 45 000 packages. Contact me and I tell you more

Adhesive Dispenser Vs. Screen Printing Adhesives Pros and Cons

Electronics Forum | Tue Oct 03 07:48:52 EDT 2000 | steveZ

Had cheacked the archives but I didn't see much about their comparison: 1. Throughput 2. Rework Rate 3. Effect on Placement Accuracy 4. Cost (cheaper or more expensive in the long term?) Has anyone compared the above. Please help me.

Re: Cooling racks

Electronics Forum | Fri Sep 22 06:59:45 EDT 2000 | jackofalltrades

For several years now we have been using a short (4 feet) conveyor with brush wheels and a simple box fan mounted under it (blowing up) to cool the product.