Electronics Forum | Wed Nov 29 14:49:38 EST 2006 | MS
Any recommendation to reduce solder beads next to 0402, 0603 and 0805 caps and res? What about home plate vs. bow tie stencil aperture design?
Electronics Forum | Fri Jul 06 13:44:15 EDT 2007 | shrek
Krikies! seems like a head-scratcher if I may say so me-self. I would say the other ogre is right, that surface finish will play a big factor in your solder joint's grain structure or how shiney 'tis. Non-HASL bearing finishes will typicaly exhibit
Electronics Forum | Wed Jun 26 17:51:55 EDT 2013 | ryansmta
Thank you for your response and interest to help me with my research work. I am actually in need of the Reel Holder. I am aware of a few services that can package the treated 0402 / 0201 components into a tape and reel. I have also spoken to MidAm
Electronics Forum | Mon Jun 24 14:52:40 EDT 2013 | ryansmta
I am in need of two Fuji or Panasonic "tape and reel" holders. I will be using them to hold dummy 0402 and 0201 outline components which have undergone some special treatment and packaged in tape and reel. This is not for SMT application but for s
Electronics Forum | Mon Oct 09 13:36:30 EDT 2006 | ppminc
Phil, The QSA-30 was built by Sam Sung, Sold by Quad. Single Head 2 Nozzles around 11K CPH Quad does not support the machine but I believe you can get parts direct from Sam Sung. I am not sure if they have a registration fee. The QSA used Quad made
Electronics Forum | Tue May 02 01:55:13 EDT 2000 | Erhard Hofmann
You are right, I am looking for a solution to place small components, 0603, 0805, 0402, and similar. The components will be fed by a vibratory feeder and placed onto trays. This is happening in the comp manufacturing stage and the trays are used as a
Electronics Forum | Wed Jul 31 14:08:22 EDT 2002 | Dave G
Used this paste on ENIG boards W/O N2 and had very good results. (0402's,BGA's,16mil FP) Never had the need to use N2 with this paste on our products. Running with N2 shouldn't hurt anything. The wetting properties should get even better than they ar
Electronics Forum | Tue Oct 10 15:14:43 EDT 2006 | mfoster
Hi Phil, Most parts are still available for the Quad/Samsung QSA-30, through Dynatech (in North America). It is actually a single gantry, 3 spindle machine with rated speed of 14,000 cph. As with any used machine, it could be a great deal or a not
Electronics Forum | Fri Jul 06 12:11:34 EDT 2007 | james
We are starting to see issues with using Kester WS R562 with lead free components. The joints look grainy on almost all of the 0402'2 and other small components. Some of the solder does not solder to the terminations. These are hybrid boards which