Electronics Forum | Tue Nov 11 16:01:09 EST 2003 | KSimpson
Adam, As for stripping the boards.. get them right to start with. Believe me you don't want to clean them. If you have to remove the coating most conformal coating brands offer a removal agent that has been tested on most all component ranges. IF yo
Electronics Forum | Mon Oct 25 17:50:46 EDT 2004 | Mike
I work for a PCB Manufacture and I am looking for info on BGA Pull test or strenght test. I have a CM that is experiencing bga's with some weak joints. they are telling me that when they do their pull test the joints are breaking at the nickel inste
Electronics Forum | Wed Feb 10 21:41:54 EST 2010 | plaiming
We experiences some failures on PCB assemblies from the field when a methacrylate epoxy adhesive was used to secure some through-hole components to pcb board as reinforcement against vibration. During application, the epoxy covered some smaller SMT c
Electronics Forum | Tue Jun 01 07:26:55 EDT 2004 | johnwnz
Alistair, your paste deposit is controlled by a few things: Stencil thickness Squeegee pressure Squeegee speed Print gap in 99 out of 100 applications for paste printing you would have a print gap of 0 i.e. on contact printing where the PCB is in fu
Electronics Forum | Tue Oct 07 12:35:10 EDT 2008 | andy_pal
Hi All, I am using COB on my DOUBLE SIDED PCB. lastly we used Eletrolytic Ni / Flash Gold Plating. Our Boards vias Failed the UL corrosion Test. we did some cross-section analysis and found 10.75 �m of Nickel and 0.022 um of Gold and as the Process
Electronics Forum | Fri Jan 15 11:40:37 EST 1999 | Bob Willis
| | I am experiencing a problem with a surface mount coax connector that over time pulls loose from the PWB. The connector has 4 small gold plated leads and we are soldering it to a flash gold board. A cable plugs into the connector and puts some c
Electronics Forum | Wed Aug 19 08:00:55 EDT 1998 | Earl Moon
| Hi there, | I'm actually facing a lot of trouble with PCB's presenting up to 3mm of bow /twist at reception i.e. before assembly. The PCB size is 220 by 230mm. The boards are to be assembeled SMD double sides with 05.mm pitch on both sides. In orde
Electronics Forum | Wed Jan 21 03:44:04 EST 1998 | Igmar
| We are currently investigating alternatives to HASL for circuit boards with 20 mil pitch smt pads and below. If you have experience with this product or simular immersion tin products with respect to manufacturing or assembly I am very interested
Electronics Forum | Sat Dec 04 09:23:20 EST 1999 | Christopher Lampron
Kantesh, Does this particular part have a heat sink across the bottom side of the component and does your pad size and stencil aperture match the component? I have just had a very similar problem with a DPAK. What we found was that the recomended pad
Electronics Forum | Wed Jun 03 09:48:47 EDT 1998 | Gary
| I have a component that is glue cured on the bottom of a pcb. The component is a 1206 size jumper. It is made up of iron/nickel alloy. The problem I am having is that the part will fall off the board during wave solder. Is the component not abl
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830