Electronics Forum | Fri Jan 22 14:31:14 EST 1999 | Dave F
| I have boards coated with Humiseal 1B73. At a late point mfg. site we need to remove a series of 0603 resistors for optioning purposes. I have been trying to determine the fastest, easiest way to re-coat the pads after removal. Drying time of the c
Electronics Forum | Mon Apr 08 14:16:29 EDT 2019 | sever_83
We've never heard of seen of such a thing either. We tried a clean sample board and applied con coat. Same process through out and we saw nothing. After speaking with the original operators who was curing the boards he had left the boards much longer
Electronics Forum | Fri Apr 22 10:12:14 EDT 2005 | davef
Common RTV does out-gas causing corrosion. NASA allows use of non/low-out-gassing RTV. Try the following companies: * Ablestik Electronic: Materials, 20021 Susana Road, Rancho Dominguez, California 90221 U.S.A., 310-764.4600, F 310-764-2545 * Arlon
Electronics Forum | Tue Feb 19 14:07:29 EST 2019 | slthomas
I figured it was just going to take a little searching to find a (more expensive) stamp that used an (more expensive) indelible ink. Not the case. Just can't find anything at all, and the stamp manufacturers say not to use any ink but what they provi
Electronics Forum | Sat Jan 23 07:08:54 EST 1999 | Graham Naisbitt
| I have boards coated with Humiseal 1B73. At a late point mfg. site we need to remove a series of 0603 resistors for optioning purposes. I have been trying to determine the fastest, easiest way to re-coat the pads after removal. Drying time of the c
Electronics Forum | Wed Jan 27 09:00:56 EST 1999 | Chris Fontaine
| | I have boards coated with Humiseal 1B73. At a late point mfg. site we need to remove a series of 0603 resistors for optioning purposes. I have been trying to determine the fastest, easiest way to re-coat the pads after removal. Drying time of the
Electronics Forum | Thu Jun 27 08:47:21 EDT 2019 | SMTA-John
Having success with Circuit Boards #432 Solvent Resistant Ink - Designed specifically for circuit boards. This medium dry ink is highly resistant to solvents .... It is also non-conducting. Note: this ink contains an aggressive solvent so should not
Electronics Forum | Tue Nov 24 05:23:18 EST 2009 | prodivegsr
Hi Davef, Thanks...Saw 1 of your thread that you posted : Thanks for providing... From davef : There are many possibilities: * Conformal coat is incompatible with surface residue on the board * Conformal coat is incompatible with solder mask on the
Electronics Forum | Wed Dec 22 02:49:37 EST 2010 | raghu
Dear Sir, Please clarify my doubt... What will happened if acrylic conformal coating is mixed with poly urathane conformal coating and mixing of this composition is used to apply for electronic PCBs Thanks & Regards, Raghuveer S.
Electronics Forum | Wed Nov 25 15:16:04 EST 2009 | sforman1
Why in heavens name are you using a heat or air cure conformal coating. Why aren't you using a 100% solids UV cure system. You would never have an issue like this Sam Forman MicroCoat Technologies