Electronics Forum | Fri Jun 04 10:02:06 EDT 1999 | Chrys Shea
| | I'm encountering a new problem at my new company that I haven't encountered before in my past life - and that's Wave Soldering VIA holes. | | | | We've been getting a rash of defects that we call in this company, "insufficient solder in VIA hole
Electronics Forum | Fri Jun 04 17:10:59 EDT 1999 | C.K.
| | | I'm encountering a new problem at my new company that I haven't encountered before in my past life - and that's Wave Soldering VIA holes. | | | | | | We've been getting a rash of defects that we call in this company, "insufficient solder in VI
Electronics Forum | Tue Jun 08 11:40:03 EDT 1999 | Steve Skinner
| | | I'm encountering a new problem at my new company that I haven't encountered before in my past life - and that's Wave Soldering VIA holes. | | | | | | We've been getting a rash of defects that we call in this company, "insufficient solder in VI
Electronics Forum | Mon May 03 18:11:10 EDT 1999 | Steve Gregory
Hi Ya' John! Here's my comeback to the points you've raised...you knew I would have a comeback, didn't ya'? |Steve, | | I see your point, and yes there are alot bigger fish to fry in |the removal or control of lead in the environment. However even
Electronics Forum | Mon May 03 18:11:32 EDT 1999 | Steve Gregory
Hi Ya' John! Here's my comeback to the points you've raised...you knew I would have a comeback, didn't ya'? |Steve, | | I see your point, and yes there are alot bigger fish to fry in |the removal or control of lead in the environment. However even
Electronics Forum | Tue May 04 14:37:44 EDT 1999 | JohnW
| Hi Ya' John! | | Here's my comeback to the points you've raised...you knew I would have a comeback, didn't ya'? | | |Steve, | | | | I see your point, and yes there are alot bigger fish to fry in |the removal or control of lead in the environment
Electronics Forum | Tue May 26 15:27:36 EDT 1998 | Dave F
| | | I'm reviewing my board fab spec. It calls for a minimum SnPb thickness of 50 microinches on HASL PWB's. I've looked at other specs that call out anything from 30 to 80 microinches, and others that just say the copper pad must be covered and s
Electronics Forum | Sat Sep 18 04:42:52 EDT 1999 | Brian
Dave, I'll respond by paragraph: | | | Brian: | | I like Ag2 also. I prefer it over both 63/37 and 60/40, if the price is not a factor. Yes, gold rips through eutectic and near-eutectic solders like habanero slathered shiitake burritos through
Electronics Forum | Fri Jun 04 15:51:36 EDT 1999 | JohnW
| | | I'm encountering a new problem at my new company that I haven't encountered before in my past life - and that's Wave Soldering VIA holes. | | | | | | We've been getting a rash of defects that we call in this company, "insufficient solder in VI
Electronics Forum | Fri Sep 17 15:01:05 EDT 1999 | Dave F
| | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However, a re