Electronics Forum | Fri Oct 01 16:17:10 EDT 1999 | Dave F
| I am currently in the middle of a company wide war and I'm looking for data (AMMO). Here are the problems: | | 1) I am looking for anyone who has done or seen any reports on Thermal Shock to smt parts and/or via holes caused by Soldering Irons at
Electronics Forum | Fri Oct 01 04:03:31 EDT 1999 | Brian
| I am having problems processing immersion gold boards. The achieved solder joints appear acceptable a la IPC-A-610, but the resultant joint does not fully cover the land, i.e. you can still see an outline of gold pad. | What is the best way to achi
Electronics Forum | Mon Aug 09 16:15:30 EDT 1999 | JohnW
| I am having cleaning problems when processing PCB's which have | TAIYO solder mask on them. After processing, hand soldering and | cleaning, a sticky residue is remains, resulting in a cosmetically poor finish with tide marks etc. Other soldermasks
Electronics Forum | Mon Aug 09 18:03:28 EDT 1999 | Earl Moon
| | I am having cleaning problems when processing PCB's which have | | TAIYO solder mask on them. After processing, hand soldering and | | cleaning, a sticky residue is remains, resulting in a cosmetically poor finish with tide marks etc. Other solde
Electronics Forum | Tue Jul 06 10:12:44 EDT 1999 | John Thorup
| | Is the no clean solder paste as good? We are wondering if we can elliminate the wash when we change from through hole to surface mount. | | | John, | | No clean is as good as your process, and the paste you are using. Everything I do is no cle
Electronics Forum | Wed Jun 30 10:37:11 EDT 1999 | Boca
We are wave soldering some fabs with a lot of unmasked trace area along the edges. The trace area is solid copper covered with tin / lead, no masking, no components along the edges, same on solder side and component side (goofy board design). Inste
Electronics Forum | Wed Jun 30 11:38:05 EDT 1999 | Brian Conner
| We are wave soldering some fabs with a lot of unmasked trace area along the edges. The trace area is solid copper covered with tin / lead, no masking, no components along the edges, same on solder side and component side (goofy board design). Ins
Electronics Forum | Wed Sep 30 13:54:00 EDT 1998 | Chrys
All y'all | | BACKGROUND. How many times do you see folks come to work all painted-up and then by the time first break comes, the lipstick, eye liner, and who knows what else are gone and they�re heading for the facilities to "freshen-up." I w
Electronics Forum | Fri Oct 02 16:52:38 EDT 1998 | Dave F
All y'all | | | | | BACKGROUND. How many times do you see folks come to work all painted-up and then by the time first break comes, the lipstick, eye liner, and who knows what else are gone and they�re heading for the facilities to "freshen-up."
Electronics Forum | Mon Jan 19 20:25:52 EST 1998 | Steve Gregory
| I have a problem! The solder on my pc boards look great comeing out | of my reflow oven. They go thrue the rest of the prossese | and at the end at the qc station it's cold or whitish or gray not shiny. | does any one have a idea on how to correct