the SOIC encounter solder crack after reliability test, the common process is: SMT---manual soldering---IPT(in process test)---potting---T/C(thermal cycling,only add current and voltage)---B/T and F/T (burn in and functional test). the condition is 2
Electronics Forum | Mon Jul 01 20:42:54 EDT 2002 | davef
Comments [questions] are: * It�s strange that an uggie ol� SOIC, 50 pitch, BIG honkin� solder pad, kinda thang is failing. Sumpin aint kosher, yano? * Where is the failure occurring [ie, lead to pad, pad to board, etc]? Talk about the breadth and di
Electronics Forum | Thu Nov 17 13:13:49 EST 2005 | Mike
Hello, Some questions.... Are you running lead free? What alloy? What�s your pot temp at? Temp of the board after preheat? Are you getting any solder in the barrels (
Electronics Forum | Wed Jun 29 17:58:12 EDT 2005 | GS
Hello, in Europe (SN100C sold by Balver Zinn) several solder pots have been filled by this alloy. On the paper I heard talking very well in terms of performance and good price, but not data are available ( as I know) about performance and if r
Electronics Forum | Thu Nov 17 20:51:16 EST 2005 | cangly
Morning Mike, We use Pb63/Sn37, Alpha Metal alloy. Solder pot is at 250 C. The profile of board after Preheat about 100 C, Lambda Wave about 220C (use both Lambda and Chip wave), DWell time 2.1s ~ 3s. Conveyor speed 1.5 in/min. We run by bare board a
Electronics Forum | Mon Jul 14 09:41:35 EDT 2008 | davef
Q1. Do we really need to follow the IPC J-STD-001 Solder purity? A1. Yes, you should control impurities in solder. Further information: * "Allowable concentration of contaminating elements in solder: impurities are harmless unless their level goes to
Electronics Forum | Fri Jan 18 15:34:51 EST 2013 | ccouture
if your solder wave machine has a removable solder pot, consider getting a second solder pot. So you will start with a brand new empty solder pot. Keep the current one with your current solder as a backup.
Electronics Forum | Mon Jun 12 07:52:21 EDT 2017 | tch
We have had this issue on our Delta 3 waves and determined that there are small pin holes in the solder pot. We had plates welded to the outside of our solder pot on the lead free wave and this bought us enough time until we could replace the wave, a
Electronics Forum | Sat Oct 08 04:24:37 EDT 2016 | aaronpainter
We are having an issue with the solder bars hanging the solder feeder dripping down the back side of the pot, and leaking in to the area where the terminal block for the elements on the pot are. We have tried aluminum tape to close off the gap betwee
Electronics Forum | Wed Jan 15 21:55:41 EST 2014 | padawanlinuxero
we do that and there's a variation on the solder temp. sometimes around 10 degrees, we have 2 solder pallets that are run in intervals of roughly 3 1/2 minutes a part (the time that take the operator to put all 3 terminals in a 42 pcbs per board, and