Electronics Forum | Wed Jul 27 16:46:48 EDT 2005 | russ
I don't think that you would need to test these. Have you ever seen any evidence of solder sticking to them? We use the same material and never notice anything besides flux staying on the bottom. Would the lead absorption if any even be of a concer
Electronics Forum | Sat May 15 11:27:26 EDT 2010 | davef
We'd expect both OSP poor wetting and improper reflow recipe to show-up in more places than just this one component. But if those are the only choices, we'll go for 'wrong solder paste.' Ooops, that's not one of the choices. Ok, OK, we'll take poo
Electronics Forum | Tue Dec 10 14:10:38 EST 2002 | Randy Villeneuve
Steve, I wave solder most if not all our boards with selective wave pallets. I did not catch if the solder balls were on top of the board or on the bottom but that will make a difference on what to do to get rid of them. Pallets are good and bad. On
Electronics Forum | Thu Dec 05 11:04:27 EST 2002 | slthomas
They're IR, bottom side only. Frankly wave solder is not my forte (there are those that would claim nothing is), but I've personally been tasked with developing a process to do reliable, high volume bottom side SMT, so I'm drawing a lot from the tec
Electronics Forum | Tue Jun 03 12:24:50 EDT 2003 | blnorman
I have received information from the European Commissioners Environmental group that automotive electronics are not covered by WEEE (waste electrical and electronic equipment 2002/96/EC) or RoHS (reduction of hazardous substances 2002/95/EC) because
Electronics Forum | Fri Apr 06 08:27:09 EDT 2001 | CAL
From what you are saying................If I hear ya correctly - There is no "Proctective" on the Pads (OSP, HASL....) You will be hard pressed soldering to bare copper. This can not be right. My suggestion- go polyimide with electroptical connecti
Electronics Forum | Fri Apr 06 08:28:34 EDT 2001 | CAL
From what you are saying................If I hear ya correctly - There is no "Protective" on the Pads (OSP, HASL....) You will be hard pressed soldering to bare copper. This can not be right. My suggestion- go polyamide with electroptical connectio
Electronics Forum | Mon Oct 29 18:21:43 EST 2001 | slthomas
We recently have received a lot of warped (bowed and/or twisted behond IPC 600 specs.) bare boards (some our fabricator's fault, some ours by design) and I can't help but figure that long term reliability will suffer when building product with them.
Electronics Forum | Fri Apr 06 08:36:13 EDT 2001 | Cal
Sorry about the double post.........my Vanna White spell check crapped out on the first reply.
Electronics Forum | Fri Aug 01 00:30:04 EDT 2003 | caldon
Also Try: http://www.airliquide.com/en/business/industry/electronics/expertise/tech_papers.asp you can also search the airliquide site for "PPM" once in the electronics section Cal