Electronics Forum | Mon Sep 14 20:19:33 EDT 2020 | kumarb
Hi. 1) recommend to phone up Heller for assistance on this case 2) using the wakeup profile, can you confirm if the problem remains or not when you skip the warm up of zone # 2? 3) each zone is based on 2 heaters (this is what we have on our 1809e
Electronics Forum | Tue Dec 29 17:21:46 EST 1998 | Dave F
| I am looking for a questionaire/list of items that need to be addressed to determine the pros/cons and equipment, manpower, cost and lead time to determine if one should consider setting up an in-house SMT line. | Can anyone help? | thanks | | J
Electronics Forum | Mon Sep 29 16:38:07 EDT 2014 | rgduval
These papers are a good place to start when learning about profiling: https://www.smtnet.com/library/files/upload/374_RSS_vs_RTS_revised_12-99_(no_pics).doc http://www.ipcoutlook.org/pdf/best_practices_reflow_profiling.pdf If you're having a lot o
Electronics Forum | Tue Sep 08 13:33:07 EDT 1998 | Brad Kendall
For pick and place, I have worked with the Zevatech machines and Philips machines. Both are great machines. The Zevatech will give you greater speed and still offer great accuracy and repeatability. Don't let the belt drive stuff scare you, it sta
Electronics Forum | Wed Mar 14 17:11:57 EST 2001 | davef
First, x-ray inspection machines have a wide range of capilities. Resolution is a key measure of a machine's ability to "distinguish" features. People say that some x-ray inspection machines have the ability to position the board being inspected at
Electronics Forum | Wed Oct 06 09:23:47 EDT 1999 | Wolfgang Busko
| I would like comments on how the industry handles 0402 parts, regarding identification. Since the parts are too small to be labeled, how can we accurately identify the parts and or values, either before or after assembly? | When the boards go to te
Electronics Forum | Sun May 16 10:11:50 EDT 1999 | M Cox
| I'm running memory module product- SMT double reflow ( 12 modules per panel). I'm using the epoxy base solder paste in order to reduce the flux spattering problem onto the gold finger which could lead to the intermittent contact problem. | | I do
Electronics Forum | Thu Apr 22 20:26:39 EDT 1999 | Dave F
| | On various PCB's after building processes,such as reflow, flowsolder and wash. The soldermask on the PCB's have become discoloured, like a 'marble' effect all along the solder side of the board, it is lighter in contrast than normal, although whe
Electronics Forum | Fri May 15 12:01:34 EDT 1998 | Justin
| | We understand that testing for ionic contamination and surface insulation resistance measure different properties. We assemble printed circuit boards for other companies. We will not get combs on 90% of the boards that we assemble. | | We have
Electronics Forum | Fri Mar 06 10:15:00 EST 1998 | Justin Medernach
| Does anyone know of a web page that provides troubleshooting techniques for the printing process? We aren't experiencing a problem right know but are attempting to set up a reference guide for training. Any help would be greatly appreciated. | Than
.gif)