Electronics Forum | Fri Jun 07 11:39:33 EDT 2019 | gregoryyork
I feared so. The only thing to be done is to tell the PCB manufacturer to increase the Thermal cure so dont set the oven to 150C but to 170C and actually measure the middle board and once it hits 155C then give it an hour cure from then. Also insist
Electronics Forum | Thu Mar 23 10:15:57 EDT 2017 | solderingpro
Rob, That is where Bob works. ------------------------------------------------------- There are many companies that exist offering multiple different products and procedures for cleaning pcb assemblies. I agree, in my practice, most companies str
Electronics Forum | Mon Mar 01 22:24:53 EST 1999 | Dave F
| It seems to be that we have to much NaCl left on our assambled PCB's. | The flux we use is from cobar. They say it can not be from the flux... So what can be the reason, what kind of problem may occer when there is to much NaCl. | George: When so
Electronics Forum | Thu Oct 15 16:41:28 EDT 1998 | Dave F
| | All Y'll | | | | How do you clean components that must be added to an assembled board after water wash? | | | | BACKGROUND | | | | Our basic process goes like this: | | | | 1 Print paste with OA flux, place, reflow, wash | | 2 Repeat 1 | |
Electronics Forum | Sat Oct 17 10:50:11 EDT 1998 | mike
| | | All Y'll | | | | | | How do you clean components that must be added to an assembled board after water wash? | | | | | | BACKGROUND | | | | | | Our basic process goes like this: | | | | | | 1 Print paste with OA flux, place, reflow, wash |
Electronics Forum | Mon Feb 27 17:08:15 EST 2006 | GS
3,5 ugr/cm2 NaCl) or power components, or Raw PCB. Nothing with the solder process or fluxes. Ion Chromatography analysis was necessary to help understanding of contamination origin. When occasionally we run TIC on a NC assembled PBA (Paste ROL0 or
Electronics Forum | Sun Jan 31 03:28:24 EST 1999 | Jeff Sanchez
| Hello Netters, | | I need some info, Earl or Dave, I have a PCB that exhibits a white layer on solder side. It does not appear to be surface residues (IPA has no effect), but looks like its under solder mask. My first guess is that the LPI solde
Electronics Forum | Thu Jan 28 14:10:57 EST 1999 | Tom B
Hello Netters, I need some info, Earl or Dave, I have a PCB that exhibits a white layer on solder side. It does not appear to be surface residues (IPA has no effect), but looks like its under solder mask. My first guess is that the LPI solder mask
Electronics Forum | Thu Jan 28 15:43:16 EST 1999 | Dave F
| Hello Netters, | | I need some info, Earl or Dave, I have a PCB that exhibits a white layer on solder side. It does not appear to be surface residues (IPA has no effect), but looks like its under solder mask. My first guess is that the LPI solde
Electronics Forum | Wed Dec 19 01:17:13 EST 2001 | ianchan
Hi Experts, I need help here, advice appreciated from all... Production is running a Lot of flex-circuit PCB, through the SMT line, with 0402 components. The flex-PCB is taped to FR4 support "pallets" when processing thru' the SMT P&P m/c. We use