Electronics Forum | Thu Dec 29 10:47:05 EST 2005 | Chris
The paper Dave posted the link for is great. I have to go back and read it in depth. I can build prototypes by wirebonding to ENIG. I can do it on a manual wirebonder but I don't have the patience to do it on a magazine to magazine automatic machi
Electronics Forum | Mon Dec 13 00:05:28 EST 1999 | Dennis O'Donnell
I can't figure out why everyone is plating everything with gold. According to the J Standard, gold plating should be removed before soldering to the surface. The gold, when left on the surface to be soldered will contaminate the solder joint and ca
Electronics Forum | Fri Apr 13 21:02:19 EDT 2007 | Sam
Anyone experience using SnPb wire to gold plated ICs? I have tried to solder the SnPb wire to the gold plated ICs lead, but the surface finishing is dull. Can anyone explain that to me? Why it is not shinny surface? Any recommendation?
Electronics Forum | Fri Nov 26 05:22:44 EST 2010 | 89jeong
Hello Esoderberg. Did you get the analyis report from your vendor? If so, could you pls share it wiht us? Based on my experiance, this issue may be caused by the Au plating. You need to ask your vendor to check the Au thickness or Au plating proces
Electronics Forum | Mon Dec 13 10:12:45 EST 1999 | John Thorup
Hi Dennis The gold plating on a circuit board is present to protect the nickle plating from corrosion. The layer is so thin that as it goes into solution in the solder it constitutes only a small percentage of the total joint. It is commonly accept
Electronics Forum | Wed Feb 04 06:26:20 EST 2009 | sachu_70
Hi Peter, The defect you observe during the second side reflow could be caused due to improper Au plating thickness in the PCB fabrication process. You can refer IPC-2221 wherein plating thicknes for ENIG mentions 0.08um to 0.23um for Immersion Gold,
Electronics Forum | Fri Nov 10 17:44:48 EST 2000 | Dave F
In response to your questions: Is the embrittlement from excess gold in lead / tin solder connections bad? It can be vereeee bad. Does it affect all plating processes the same? Give us a break and read the SMTnet Archives, for instance: BGA prob
Electronics Forum | Mon Feb 09 16:55:28 EST 2009 | cuperpeter
Hi Sachin, thanks for your feedback. According to our supplier, surface plating is electrolytic gold over Nickel(not ENIG), but I think that is a still improper thickness for Au. (according to 3rd Working Draft from September 2008 of IPC 2221B "0.4
Electronics Forum | Wed Jan 09 14:52:53 EST 2002 | Chris
Hi, I have read many articles about theromsonically bonding to soft gold. Many of these articles state you can bond to 10uinches of gold. I have worked with both Hughes and Panasonic bonders at two different companies and I have never been able to
Electronics Forum | Mon Jan 07 13:18:28 EST 2002 | mregalia
I work for a microwave company. On our lower frequency boards (