Electronics Forum | Wed Jul 09 16:01:10 EDT 2003 | russ
Mike, the one pad that is "small" definitely appears to be over etching (It looks like it was supposed to be much larger). What is the dims of this little bugger as compared to the Gerber? i would also tend to believe that there probably is some mask
Electronics Forum | Tue Jul 28 07:02:59 EDT 1998 | smd
Right now we are taping the goldfingers which is effective but also expensive. Also, some tape was leaving yellow marks on the goldfingers. We're trying the so-called goldfinger glove from Steven's Products. It's a very small company (probably one gu
Electronics Forum | Mon Aug 03 08:29:24 EDT 1998 | Dave F
SMD: Sounds interesting. What is the contact information on Steve? Dave F | Right now we are taping the goldfingers which is | effective but also expensive. Also, some tape was leaving yellow marks on the goldfingers. We're trying the so-called go
Electronics Forum | Mon Aug 03 08:23:37 EDT 1998 | smd
Stevens Products (supposedly around since 1937) 128 N. Park St. E. Orange, NJ 07019 Tel 973-672-2140 Contact: Ross Stevens, Jr. They'll take a PO but terms are net 30 Right now we are taping the goldfingers which is | effective but also expensive. A
Electronics Forum | Wed May 30 17:49:49 EDT 2001 | davef
You are correct. IPC wants you to pay for that standard, regardless if you get a hard copy or download it. Generally, it�s pretty boring stuff for production types. [Although, you will recognize some of the goofy things your designers have done to
Electronics Forum | Fri Mar 23 09:28:46 EST 2001 | PeteC
Well, it's hard to say what it started out as, a smear, splash or ball cause the solder formation on the finger after reflow is spread out ya know. I looked at an archive for possible causes and one was printer operators with paste on their fingers.
Electronics Forum | Fri Oct 02 16:52:38 EDT 1998 | Dave F
All y'all | | | | | BACKGROUND. How many times do you see folks come to work all painted-up and then by the time first break comes, the lipstick, eye liner, and who knows what else are gone and they�re heading for the facilities to "freshen-up."
Electronics Forum | Fri Jul 10 09:56:11 EDT 1998 | Justin Medernach
| I am looking for some guidelines on evaluating solder paste. I am specifically interested in No-Clean Pastes, as they are a completely new ball game when it comes to slump, tack time, stencil life, tack time, etc. | Thanks for any and all help give
Electronics Forum | Wed Apr 21 17:08:32 EDT 2004 | dave
Congratulations on your new customer. This could be a keeper. Here's what you're familiar with: Electroless Nickel - per MIL-C-26074 and ASTM-B733. Electroless nickel describes the plating of nickel deposits, which may contain phosphorus and boro
Electronics Forum | Fri Oct 14 11:56:49 EDT 2005 | patrickbruneel
Mika, 1.) Is there a maximum board thickness where it would be almost impossible to get a decent hole fil? Answer: The thicker the board the further the solder has to travel and the more you depend on solderability of boards and components, machine