Scott, I am not really in a position to answer this as fully as I would like because most military work with which I am familiar is subject to some degree of secrecy most especially on the internet. At least we have signed up to such restrictions. Ho
Electronics Forum | Thu Nov 17 21:46:48 EST 2005 | C. Kolokoy
With DIP type components, a sub-par fluxing method (foaming a no-clean), and a chip wave where one is not needed are formulas for bridging and insufficient wetting. If you have SMD's on the wave solder side of the board greater than 0603, and no SOT
Electronics Forum | Tue Apr 01 09:03:39 EST 2003 | kmorris
Hi: I'm looking for input from anyone who has experience assembling the MLP package on PCBs. We are experiencing solder opens after assembly, and I'm curious to see how others are processing these critters. The part we are using is a Semtech SH3000
Electronics Forum | Mon Oct 16 20:29:32 EDT 2000 | Dave F
Jason: How did you determine that the deposits are tin oxide? What does this stuff look like? Klein Wassink "Soldering in Electronics" (p. 221, quoting original work by others). States (in effect) tin (or solder) quickly forms a protective oxide
Electronics Forum | Tue Sep 15 10:43:25 EDT 1998 | dave c
| Dave, | Sounds like you have material issues. Been there, done that. Tried 'em all. The best, longest lasting material I've found is called Durostone. It's made by a Roeschling, and most of the big fixture cutting houses now offer it as an option
Electronics Forum | Fri Apr 03 08:22:36 EST 1998 | Scott Cook
| At this moment in time we are using water soluble solder paste on our PCBs these are cleaned using water only, agitated with ultrasonics. After drying a white/grey residue is left around solder joints. Reflow profile is fine and a reliable wash pro
Electronics Forum | Sat Jul 02 10:27:19 EDT 2022 | madisreivik
Hello ! I got exp only with leadfree HASL, but maybe the same problems apply. Also, the leaded HASL has probably lower process temperature. This could be copper, which has settled to the tank bottom. With leadfree, the copper is removed from molten
Electronics Forum | Tue Apr 14 15:42:45 EDT 1998 | Scott Cook
| Scott, | I am not really in a position to answer this as fully as I would like because most military work with which I am familiar is subject to some degree of secrecy most especially on the internet. At least we have signed up to such restrictions
Electronics Forum | Thu Mar 28 16:00:31 EST 2002 | bschreiber
Hello Dave, Water Washable (Organic Acid, OA) post solder flux residue is designed for cleaning in plain water without cleaning chemical additives. The real advantage of water washable flux was that it cleaned in plain water without additives � no
Electronics Forum | Fri Nov 27 09:00:48 EST 1998 | Christopher Lampron
| Hi | I have been conducting my first reflow profiles. Most of the texts that I have read suggest soldering the thermocouples to a populated pcb. I am finding this very difficult. I have been using a high melting point (Sn5 / Pb95) solder and the