Electronics Forum | Tue Sep 17 15:40:59 EDT 2013 | 18424
Good day all, I wanted to get a quick poll from the folks running SAC305 in their selective soldering equipment. How are final results? How repeatable is the process, any machine related failures? pumps? nozzles? etc... I am just looking to get a
Electronics Forum | Tue Sep 17 15:47:04 EDT 2013 | 18424
Good day all, I wanted to get a quick poll from the folks running SAC305 in their selective soldering equipment. How are final results? How repeatable is the process, any machine related failures? pumps? nozzles? etc... I am just looking to get a
Electronics Forum | Tue Sep 23 23:19:34 EDT 2003 | RLW
If you have a board that you've run several times, now you run it and like before all settings are the same, but now you have 0603's randomly skewed or an inch or so away from their intended pad (as if popped up in the air), or an occasional 7343 cap
Electronics Forum | Wed Sep 18 14:12:40 EDT 2013 | pjchonis
Hello Bachman. SAC305 is the most common lead-free solder alloy, not only for wave soldering but also selective. Most of our selective customers (especially automotive) are using SAC305. What is more important than the alloy to consider is the flux
Electronics Forum | Mon Jun 26 23:33:20 EDT 2006 | KEN
We saw this condition over 3 years ago. It sometimes is called "champagne bubbles". The intemetalic formation is interrupted due to the micro voiding reducing mechanical strength. I discovered this on lead free test vehicles for a major computer
Electronics Forum | Thu Nov 02 04:42:48 EDT 2023 | tinaheussaff
In general, it is safer to use a single alloy with a known composition and performance characteristics. If you need to change the alloy used in your selective soldering machine bath, it is advisable to consult with the manufacturer or a soldering exp
Electronics Forum | Tue Nov 20 17:07:20 EST 2007 | kennyrebbe
I am looking for a new semi automatic Stencil printer, and reflow oven that is capable of doing double sided boards with BGA�s. We currently own a Manncorp 4500R stencil printer https://www.manncorp.com/4x00_stencil_printers/index.php?view=overview&a
Electronics Forum | Thu Mar 12 06:37:48 EDT 2009 | gregoryyork
I agree you are too cold for the profile get it up to 230C and possibly allow it to dwell a little longer in preheat as opposed to pushing up the reflow zone only. Sn90/Pb10 melts at 220C so 2C hotter than your profile so you are reliant on it alloyi
Electronics Forum | Wed Aug 21 17:44:32 EDT 2002 | davef
Splitting hairs, I expect SIR of all solderability protection, including OSP, to decrease after reflow. What�s more, I expect the SIR of all solderability protection to pretty much decrease over time. The �comb pattern� test specimens meet requirem
Electronics Forum | Mon Jul 12 11:35:27 EDT 2004 | Pierre RICHARD
Here are some answers to my questions after a good research. I also added more definitions that could help understand this esoteric language used in assembly, specially surrounding fluxes and their use. In blue italics are comments and extracts from