Electronics Forum | Tue Apr 17 10:16:42 EDT 2001 | davef
Welcome to SMTnet. Awww, those assemblers are always whining about something. Just tell him to shut-up and build the blankin� boards. Jeesh!!! We used to have copious archives on the topic on SMTnet and our friend Brian is working his fingers t
Electronics Forum | Mon Dec 11 20:44:37 EST 2006 | davef
Title : LEAD-FREE WAVE SOLDER FLUX EVALUATION Author : Michael Havener Author Company : Benchmark Electronics, Inc Date : 09/25/2005 Conference : SMTA International Abstract : The European Union�s deadline to ban lead in electronic pr
Electronics Forum | Fri Jan 19 17:43:30 EST 2001 | davef
Intermetalic Layer (IL). A compound formed at the interface of two different metals, whose atoms have an extremely high natural attraction for each other, so high, that they do not bond to other elements by any other means. Also, intermetalic compo
Electronics Forum | Tue Apr 03 22:03:18 EDT 2001 | davef
With friends like you, who needs enemies? I�d guess that the perceived benefits of flat pads for your 20 mil pitch and below components counter-balance the higher cost, gold being a solder pot contaminant, limited solder mask compatibility, potentia
Electronics Forum | Mon Jun 25 20:39:08 EDT 2001 | ianchan
Hi mate, no complete info given from what i see, so just some humble comments, mayhaps you review : 1) PCB pad finishing - Copper+nickle plated? coz if so, nickle is a KILLER to good solder wetting. what we did back here, was to HAL coat the nickle
Electronics Forum | Tue Dec 14 17:02:04 EST 1999 | John Thorup
Hello Kris If you do have and OSP coating I'd say Curtis has nailed it. But you seem to have references to gold. Does this board have a standard nickle/gold finish. If so what sort of "solder on gold" problems were you having? Reading between the
Electronics Forum | Fri Sep 10 14:32:49 EDT 1999 | John Thorup
| We have a product, with various PWBs, with over 600 parts each one (We are a low Volume/high mix company with an average component placement per PCB between 250 to 300 parts). This PWBs have 7 to 10, 20 mils pitch parts. We are having problems with
Electronics Forum | Mon Jul 19 11:11:18 EDT 1999 | Wolfgang Busko
| Perhaps a little hard to find but is there anyone who uses a vapor phase process to solder populated card with BGAs. I am interested in the success rate of such a process. It is obvious that the throughput is reduce vs a convection oven but still t
Electronics Forum | Mon Jul 19 11:50:47 EDT 1999 | Mario
| | Hi, SMTASSY | | that�s what we do, soldering our double-sided-finepitch-BGA-and all-the-other-stuff-boards in vapourphase because it�s the only thing we have. | First, we do not do real series produktion, only prototyping up to sometimes 20 uni
Electronics Forum | Fri Apr 16 11:07:53 EDT 1999 | Vic Lau
| | We process both tin/lead plated boards and gold plated boards in our surface mount group. I have used Sn62/Pb36/Ag2 solder paste on all gold plated boards to help prevent gold scavaging. To reduce the amount of different solder pastes we have t