Electronics Forum | Wed May 19 14:12:53 EDT 1999 | Glenn Robertson
| Folks, | I am interested in knowing what level of Nitrogen purity you are running in your reflow ovens for standard SMT assembly? | It seems over the last several years people are increasing the Oxygen level in thier reflow oven atmosphere. | What
Electronics Forum | Fri Jul 10 09:56:11 EDT 1998 | Justin Medernach
| I am looking for some guidelines on evaluating solder paste. I am specifically interested in No-Clean Pastes, as they are a completely new ball game when it comes to slump, tack time, stencil life, tack time, etc. | Thanks for any and all help give
Electronics Forum | Mon Nov 06 14:00:45 EST 2006 | nodlac
Checks calendar ...nope not April 1st. -The fresher the paste the better the solder joint. Agreed - My dilema here is upper management wants the two lines to share one stencil printer thus saving the cost of purchasing a second printer. They propos
Electronics Forum | Thu Apr 29 10:02:07 EDT 1999 | Chrys Shea
| Anyone using hot air nife for wave soldering process. | Does it work? | Does it really eliminate solder bridging and does it create any other problems? | | any feed back will be much appriciated. | | Thanks | | Tony A | | Tony, The hot knif
Electronics Forum | Thu Mar 17 11:15:26 EDT 2011 | circleprime
I did some investigating and it seemed that getting a reflow oven with an inert atmosphere could be the answer to the inconsistant wetting issues that we are having with a leadfree DFN-10 on one of our products. Here's my question(s). It seems that
Electronics Forum | Wed May 12 20:43:53 EDT 1999 | Earl Moon
| Folks, | I am interested in knowing what level of Nitrogen purity you are running in your reflow ovens for standard SMT assembly? | It seems over the last several years people are increasing the Oxygen level in thier reflow oven atmosphere. | What
Electronics Forum | Fri Jul 17 01:39:07 EDT 2009 | grahamcooper22
Hi, it is not necessary to store MSDs in nitrogen to stop them absorbing moisture, just a dry environment. Nitrogen storage is good for storing devices for many years as it reduces the oxidation of the solderable surfaces. Best option for storing MSD
Electronics Forum | Thu Apr 29 12:20:23 EDT 1999 | Tony A
| | Anyone using hot air nife for wave soldering process. | | Does it work? | | Does it really eliminate solder bridging and does it create any other problems? | | | | any feed back will be much appriciated. | | | | Thanks | | | | Tony A | | |
Electronics Forum | Sat Mar 04 05:55:40 EST 2023 | jrogalski88
So we have 3 new ITW/EAE Centurion ovens that all have issues when running nitrogen to keep the o2 ppm below 1000. It is always much higher, sometimes gets lower when no boards are loading in. They've had us replace valves and do an upgrade kit that
Electronics Forum | Mon Oct 16 20:29:32 EDT 2000 | Dave F
Jason: How did you determine that the deposits are tin oxide? What does this stuff look like? Klein Wassink "Soldering in Electronics" (p. 221, quoting original work by others). States (in effect) tin (or solder) quickly forms a protective oxide