Electronics Forum | Wed Aug 10 07:55:21 EDT 2005 | ajaydoshi
we are using heareous F381, F352 no clean solder paste. specially in qfp for high frequency board we observe that cleaing / removing of ' no clean flux 'is require. if we do not clean same most of time after all test & envioumental test it shows pin
Electronics Forum | Mon Jul 26 19:32:03 EDT 1999 | Steve Gregory
| Can anyone give me the virtues of SMT package castellations vs. no castellations with particular reference to the ruggedness and reliability of the solder joints? Any references or studies that you can point me to? Also, although I'm in favor of
Electronics Forum | Mon Aug 28 15:34:19 EDT 2000 | Steve Harshbarger
Hello Ramon, This is a very common problem that usually can be overcome. Can you tell me the flux type you are using (manufacturer, and flux number)? Has your board vendor, or type of PCB's changed (are they entec coated - bare copper)? What is t
Electronics Forum | Wed Aug 30 09:56:37 EDT 2000 | NLykus
Hi Ramon, We have had this problem before on our Seho Wave Solder Machine. We are currently using a spray fluxer as well. By imersing the PCB into the flux you stated you are getting good results. What you need to do is check your spray patter
Electronics Forum | Wed Mar 24 10:43:59 EST 1999 | Tim
Hi, I have a customer who's electronic assemblies produce RF. He is insisting upon aqueuos cleaning. We switched to a no clean solder years ago and no longer have an aqueous system. Is aqueous cleaning necessary to eliminate 'cross talk' of the s
Electronics Forum | Wed Aug 10 08:10:39 EDT 2005 | davef
Comments are: * Sounds like it's necessary to clean "heareous F381, F352 no clean solder paste" in your application. Consider a paste that may be better suited to your application. * If you're cleaning "low residue flux", consider using an organic ac
Electronics Forum | Thu Sep 26 20:43:51 EDT 2002 | davef
"OK. If the connection doesn't look like I expect it to look, how do I know that the metallurgy is correct?" Comments are: * There are no pictures that will get you though this. * You should expect that gold that is dissolved in Pb/Sn solder to make
Electronics Forum | Tue Sep 02 14:59:41 EDT 2008 | hermes
if two boards with different solder masks give different results on flux residue level after soldering with the exact same machine settings than it is clear that one of the solder masks is not compatible with your no-clean flux. could be the solder m
Electronics Forum | Fri Sep 05 13:49:04 EDT 2008 | gregoryyork
Tell the board shop to increase the cure temp of the resist as it is undecured especially if you have waxy/greasy resiues on the board and a brown tar like substence in the solder wave itself. If undercured then solder will not flow off the resist pr
Electronics Forum | Thu Aug 28 11:02:28 EDT 2008 | omid_juve
we have two similar pcb from two different pcb manufacturer one of them passed the wave soldering without any short circuit and residue and another one passed it with many residue . don`t you think that the type of solder mask from these two pcb manu