Electronics Forum | Mon Aug 04 09:30:16 EDT 2008 | grics
If you have concerns, you can look at the datasheet for each component or contact one of their application or materials engineers and find out what the components are rated for...process-wise. IE, how long can I be in the oven with this part, at what
Electronics Forum | Wed Apr 21 14:32:52 EDT 2010 | remullis
These ovens maintain good profiling as long as you stay on top of maintenance. I had 4 150's and 1 125. The biggest headache is keep the plenums cleaned (very messy). Also the blower motors have been replaced a few times on them as well. If I were yo
Electronics Forum | Thu Nov 15 09:29:29 EST 2012 | anvil1021
Maybe this piece of information will help. In China (just returned from visit) there are many factories that are using a dual temperature process using SAC305 or Sn100C and 42/58. Apparently this allows them to run their through hole parts through re
Electronics Forum | Fri May 15 21:39:48 EDT 2015 | jlawson
Reflow.. 1.Rehm (Germany) - Best in Class Best overall process stability heating system ( Alot of makers have started to copy there VX heating arrangement ). COnveyor chains can be a bit more attention in terms of maintenance on rehm , but if foll
Electronics Forum | Wed May 20 22:45:18 EDT 2015 | dinhhuunam
Hi Cohlmann, I'm Recommendations for You SJ INNOTECH PRINTER . sj is Global NO.1 Vision Screen Printer High Performance ,Vision Screen Printer & Best Solution & Service for You Detail Please Refer the Spec in Website http://sjinnotech.com/ht_ml_eng/
Electronics Forum | Wed Jun 16 20:27:14 EDT 2021 | bradleycramond
Hi Guys We looking to purchase a second hand system consisting of a Juki KE-2050L and a SMT XXS reflow oven. This will be our first system and used only for our own boards. We hoping to get some opinions and insight from others that have experie
Electronics Forum | Fri Jul 25 15:54:22 EDT 2008 | pcbbuilders
I am trying to optimize my reflow profile. i have a 5 zone oven. lead-free: for the 1st 3 zones, i am good, at about 150-200 deg for 150 seconds. during the 4th zone, i am at a temp of 200-220 for 50 seconds. during the 5th zone, i am at 220-245 f
Electronics Forum | Mon Jan 15 15:33:41 EST 2001 | davef
First, we have never repackage devices, as you propose. Our schedule has us standing at Receiving like panting dogs waiting for the material required to jump the job, much less giving up the time and money to have parts repackaged. Second, fabricat
Electronics Forum | Tue Apr 11 10:30:46 EDT 2000 | Jeremy Smith
I am having a problem with some joints on a 100 pin pqfp and few different soics on one particular board. When viewed a 8x with a "Mantis" inspection scope the joints look as though they wetted to the ic leg but when probed the leg will pop loose.
Electronics Forum | Wed Feb 09 21:29:28 EST 2000 | Dave F
Charlie: People cure glue using their paste reflow profile all the time. And most of them are happy. Personally, I�m with Dean and Travis. It�s possible to as you suggest, it�s appealing not to mess with your oven profile, but it just doesn�t s