Electronics Forum | Tue Dec 02 08:40:27 EST 2003 | Daniel Werkhoven
Dear Tom, As manufacturer of solder chemicals for the electronic industry we know we can help you out with your problem. To go no clean you most only organise that the chemistry that stays behind on yr PCB will not cause any problem during the life o
Electronics Forum | Wed May 27 09:56:39 EDT 1998 | Chrys
| | | We recently made the switch to no-clean and the wurface mount is turning out beautifully. However, the wave solder process continues to put up a fight; we are getting a white residue on the surface of the PCB. The residue is not localize
Electronics Forum | Wed May 27 15:09:30 EDT 1998 | Dave F
| | | | We recently made the switch to no-clean and the wurface mount is turning out beautifully. However, the wave solder process continues to put up a fight; we are getting a white residue on the surface of the PCB. The residue is not locali
Electronics Forum | Thu Sep 05 18:15:15 EDT 2002 | pjc
There are chemistries out there that will solublize some post-solder NC flux residues. I have had success with Zestron material Vigon A200 and Petroferm material Hydrex DX. Go to http://www.zestron.com and http://www.petroferm.com These are chemical
Electronics Forum | Tue Nov 24 19:07:12 EST 2009 | gregoryyork
I agree Patrick many people blame the assembly fluxes when it is some other hygroscopic chemistry left on the bare PCB such as surfactents from the HASL process these will do exactly what the guy reported in his post fail then cool down and pass ever
Electronics Forum | Fri Mar 26 11:48:45 EST 2004 | patrickbruneel
I know it is not easy to quantify zero. The biggest dilemma the no-residue technology is facing "disbelieve" The most accurate proof to the fact that all solids disapear under heat is TGA analysis. Test the no-residue in your facility under the rig
Electronics Forum | Mon Feb 27 16:37:57 EST 2006 | davef
Options are: * Find a low residue flux and conformal coating material that are compatable, so that cleaning is not required. * Use a cleanable low residue flux, clean according to the supplier's recommendations, and then coat boards.
Electronics Forum | Tue Oct 23 10:41:36 EDT 2012 | blnorman
Ideally first you need to analyze the residue to see what it is. We had a customer with white residues after wave and elemental analysis revealed tin.
Electronics Forum | Mon May 26 11:02:17 EDT 2008 | jandon
Hi Mr. Necdet Ozyonum, Recently we did have same kind of problems when we use lead free reflow profile for leaded solder paste (AIM WS-483). There where solder resist lacks, we found white residue after aqueous cleaning. Not in the solder joints but
Electronics Forum | Fri Oct 16 13:11:49 EDT 1998 | Steve A
The Kyzen product was brought to my attention from a chemist at Kester solders when I asked him what could remove no clean residue from a PCB that had been built weeks earlier. We soaked it in the Kyzen for 8 minutes and ran the board through the aq
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830