Electronics Forum | Wed May 27 14:20:43 EDT 1998 | Earl Moon
| We recently made the switch to no-clean and the wurface mount is turning out beautifully. However, the wave solder process continues to put up a fight; we are getting a white residue on the surface of the PCB. The residue is not localized to
Electronics Forum | Wed Jul 07 13:56:57 EDT 2004 | Pierre RICHARD
As converting our boards to lead-free finish (Immersion White Tin) we decided to change de mask color from green to blue. We thought this would be a good idea to spread the idea so we could easily recognize the type of solder application related to t
Electronics Forum | Fri Nov 05 18:47:31 EDT 2010 | eadthem
I'm guessing when you say bare board you mean wet paste only? When you say the pads move slightly are your boards warped at all at the Vscore? What we do is use per modual fids. first you delete or don't make panel fids and then theres a option wh
Electronics Forum | Thu Aug 12 09:02:08 EDT 1999 | Gian.D
| Hello, | | Could be that touchup operators are using too much flux. What are you dispensing flux with. Disposable or refillable flux pens are good to have around. | |Good! could you suggest some suppliers name or address or web site or e.mail...
Electronics Forum | Fri Aug 28 18:57:49 EDT 1998 | Mike Cleary
Selecting the correct label solution for SMT labeling is a science. Our company is a supplier of electronic identification products. Please let me know if you have questions regarding materials, printers, etc. I have been in this industry for over
Electronics Forum | Thu Sep 11 15:23:31 EDT 2003 | Peter L.
I have come across a rash of failed assemblies that have 0805 capacitors and resistors, bottom side glued, wave soldered and washed. Trouble shooter reported touching up the solder joints on a few areas and the boards would pass test. I had a look a
Electronics Forum | Tue May 26 15:53:39 EDT 1998 | Chrys
| We recently made the switch to no-clean and the wurface mount is turning out beautifully. However, the wave solder process continues to put up a fight; we are getting a white residue on the surface of the PCB. The residue is not localized to
Electronics Forum | Tue May 26 16:35:53 EDT 1998 | Ryan Jennens
| | We recently made the switch to no-clean and the wurface mount is turning out beautifully. However, the wave solder process continues to put up a fight; we are getting a white residue on the surface of the PCB. The residue is not localized
Electronics Forum | Thu Feb 07 12:37:42 EST 2013 | phase1
Resistor/Caps using package library Match-45% White pixel solder-25% search window-25% Tant caps custom teach checking for pattern/value Do you also put a polarity band check in there or just check the value and click the polarity box? same passing
Electronics Forum | Sat Feb 05 09:08:18 EST 2000 | Dave F
Casimir: Let me expand on something that I said in my response to your thread on ionic testing. Generally, no-clean people don�t use ROSE testing as part of their process control, because the ROSE test is essentially washing your board in DI/IPA �