Electronics Forum | Fri Jun 19 13:40:25 EDT 1998 | Terry Burnette
| Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | Mike There has been a
Electronics Forum | Mon Sep 11 14:07:26 EDT 2000 | Steve
Hi ya'll!! We've got some PCB's in receiving inspection that has these little nodules in plating inside all of the barrels. These are microwave PCB's and have almost all of the surface area on both sides covered with with solid metal planes, and no
Electronics Forum | Tue Dec 13 14:55:12 EST 2005 | muse95
Your response is from the point of view of using a Bismuth solder with Pb plated leads. Samir's point of view is from Bismuth in the plating on the leads being used with a Pb solder. There is a very large difference in the amount of Bi that will en
Electronics Forum | Thu Mar 02 21:17:41 EST 2000 | Dave F
Dave: It's good to know what that stuff is. With your NiO, you have the typical ENIG problem. I can imagine some causes for your disaster: * too thin gold plating * oxidized nickel under gold plating * porous nickel plating * wrong soldering pr
Electronics Forum | Thu Oct 26 18:43:09 EDT 2000 | Christopher Noonan
I am looking for tooling plate manufactures. I am kind of new to the SMT process, well as far as tooling goes, and I am trying to find a machinist to make tooling plates for Fuji and Siemens placement machines. Does anyone have any recommendation f
Electronics Forum | Mon Oct 23 21:05:37 EDT 2000 | cklau
If you're looking for PWB cleanliness , please consider one surface treatment other than HAL (i.e HRF-heat resist flux). HRF is a very inexpensive and effective process that your board manufacturer can provide you to meet your requirement. For gold
Electronics Forum | Thu Mar 02 21:17:41 EST 2000 | Dave F
Dave: It's good to know what that stuff is. With your NiO, you have the typical ENIG problem. I can imagine some causes for your disaster: * too thin gold plating * oxidized nickel under gold plating * porous nickel plating * wrong soldering pr
Electronics Forum | Mon Oct 25 15:56:56 EDT 1999 | Dave F
William: Three things: 1 If the gold is porous, it will not protect the nickel and the nichel wiil oxidize and become unsolderable. 2 If the nickel is not solderable, the gold overcoat will not improve that. 3 Ag or Au over electroless Ni creates b
Electronics Forum | Fri May 28 15:50:48 EDT 1999 | Frank Boyko
We now put soldermask on copper and then immersion nickel/gold plate our fine line boards. One of our vendors says this causes skipped plating in small via holes and wants to nickel/gold plate the whole board, including via holes, and then apply sold
Electronics Forum | Fri Jun 19 14:25:24 EDT 1998 | Earl Moon
| | Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | | Mike | There has b