Electronics Forum | Thu Aug 19 19:04:55 EDT 1999 | Brian Wycoff
| | Can anyone help on the subject of de-wetting during the spray coating process. We use PC29M Parts A+B spray coating material, Humiseal tapes and masking dots, Marigold supertouch V70N gloves and Concoat CM533 liquid masking material. We also use
Electronics Forum | Tue Jul 25 16:08:52 EDT 2017 | dontfeedphils
I'm currently working on bringing a manual coating process/workcenter online and my QA team is giving me some grief. For background, we're using Humiseal 1B31 thinned with thinner 521, mixed at 1:1 by volume. Spraying through a Binks HVLP with 10 P
Electronics Forum | Mon Jul 18 12:24:53 EDT 2016 | oleksz
Some people involved in PCB assembly process claim that SMD components reflow soldering problems are often caused by traces running under a component. According to this claim, trace (or any copper) covered by solder mask and placed under SMD componen
Electronics Forum | Mon Jul 18 12:25:30 EDT 2016 | oleksz
Some people involved in PCB assembly process claim that SMD components reflow soldering problems are often caused by traces running under a component. According to this claim, trace (or any copper) covered by solder mask and placed under SMD componen
Electronics Forum | Mon Apr 17 19:44:20 EDT 2000 | Dave F
Ashok: Well, your customer probably has a good reason for wanting you to send them boards without holes in the solder mask. What is their goal for the mask capabilities after you get do reworking the boards? * Cosmetic surface coat? * Performance t
Electronics Forum | Fri Aug 21 07:57:20 EDT 1998 | Earl Moon
| | | Will somebody please explain HASL (here). Thanks. | | Tryin: HASL: Hot Air Solder Leveled. A board fabrication process that applies an oxidation preventing solder coating to copper pads on the board. Dave F | You do this to keep the green s
Electronics Forum | Tue Nov 07 02:50:41 EST 2000 | CharTrain
A solder wetting balance will indicate a time of less than one second for wetting to occur to a solderable surface. The additional time is required to get the metalized surfaces up to soldering temperature. A single sided board has very little mass a
Electronics Forum | Thu Jul 17 20:46:55 EDT 2008 | davef
Which type? * Solder beads (mid-chip solder balls, attached to the waste line of your chip caps and resistors) This is more paste volume related. * Solder balls that tend to be more randomly scattered (as in spattered)? This tends to be more profile
Electronics Forum | Tue May 06 22:54:08 EDT 2003 | davef
tommyg_fla. Sorry about being late getting back you. Surface-active species, such as Fe2+, Mn2+, NH4+, and H+, can be adsorbed onto solid phases [and transported by things as weird as bioturbation or advection not that they have anything to do with
Electronics Forum | Tue Mar 30 02:58:55 EST 2004 | Grant Petty
Hi, Thanks for the ideas. With the solder mask curing problems, can you normally wipe off the white residue, as we can do this on our boards with our fingers. It's almost like the surface of the board has a "wet dried up" look to it, and it's a smok
The SMTA membership is a network of professionals who build skills, share practical experience and develop solutions in electronic assembly technologies and related business operations.
Training Provider / Events Organizer / Association / Non-Profit
6600 City W Pkwy
Eden Prairie, MN USA
Phone: 952-920-7682