Electronics Forum | Wed Dec 08 04:19:16 EST 1999 | pascal MATHIEU
I am working in electronic automotive industry and today we are facing to a very serious problem : if we want to use a PCBoard with a copper thickness of 90�m + fine pitch circuit (0.65mm, 0.5mm) the supplier(several) of the PCB has some trouble t
Electronics Forum | Fri Jan 15 11:25:29 EST 1999 | E. R.
Does anyone have information pertaining to re-balling BGA components using balls that are preformed onto disolable paper waffers (mini BGA reballing kit)? The paper containing the specific BGA device/pattern would be placed onto the BGA then process
Electronics Forum | Thu May 28 21:13:09 EDT 1998 | skhun
| Our company is currently looking to implement a SMT production line. What I am looking for is feedback on people's experiences with various machines. | Here's what we are in the market for: | Low/Mid volume 3,000+cph machine that can handle high j
Electronics Forum | Wed Jul 07 13:56:57 EDT 2004 | Pierre RICHARD
As converting our boards to lead-free finish (Immersion White Tin) we decided to change de mask color from green to blue. We thought this would be a good idea to spread the idea so we could easily recognize the type of solder application related to t
Electronics Forum | Sun Oct 24 11:20:57 EDT 2004 | sagan
Hello everyone. The company i work for owns a PM570L and a PM460. The PM460 recently came from service repairs and it has a problem that me and the technicians at Zevatech AG are trying to solve but i would like to hear from anyone with experience o
Electronics Forum | Thu Apr 21 11:43:03 EDT 2005 | davef
We understand the problem of trying to coat over RTV. We have seen the same problem with acrylic and urethane coatings not wanting to stick to RTV. Some acrylics seem to be worse than urethane. Since this is a new product, may be you could pot your
Electronics Forum | Mon Jul 03 05:39:05 EDT 2006 | ronalds
Hi, I am experience problems while testing wave soldering SMT components that are glued on the solderside (lead free). Between de leads of SOx type IC's and SOT's develop a great deal of solder beads. I have been using a RSS temp.profile while spr
Electronics Forum | Tue Aug 22 03:04:07 EDT 2006 | PP
Any help/suggestion is much appreciated I am doing lots of BGA Reworks from a small uBGA with a few balls to a large BGA with over 1500 balls. The reworks have been done on SRT 1100 Series Machine for many years. SRT 1100 Machine is good for the c
Electronics Forum | Fri Mar 26 11:31:34 EDT 2010 | rway
I have been using ICT for a number of years. It is still a viable resource for catching defects in the production process. AOI doesn't catch everything, such as bridging on QFN or J-lead devices (this will depend on the type of AOI and camera syste
Electronics Forum | Tue Feb 15 00:27:39 EST 2011 | jeffr
First clean and de-bur the hole in the nozzle, then try it again. If the Head does not pick up at the feeder, then moves to the dump position...it means that the Vacuum Sensor Board has detected that the nozzle vacuum is above the LOW threshold setti