Electronics Forum | Thu Nov 17 21:46:48 EST 2005 | C. Kolokoy
With DIP type components, a sub-par fluxing method (foaming a no-clean), and a chip wave where one is not needed are formulas for bridging and insufficient wetting. If you have SMD's on the wave solder side of the board greater than 0603, and no SOT
Electronics Forum | Thu Nov 17 08:57:39 EST 2005 | russ
No clean and foam fluxing is not a very good process from my experience. I know that the flux manufacturers claim that they are suitable but I am not sure what "suitable" means. I would bet that you have very inconsistant flux coverage. How often
Electronics Forum | Tue Feb 19 15:28:05 EST 2002 | gtemple
Check the pcb layers. Maybe it gets hotter in certain areas of the board. Most parts being wave soldered should be clinched, crimped whatever to avoid this. What parts are lifting?
Electronics Forum | Wed Nov 01 12:04:46 EST 2000 | JohnW
Adam, Didn't we do this already?, check the archives, I've discussed rotational carriers before. You can use them fo setting up an designing the pallet but you can't use them for mass prouction, for one your waisting valuable pallet space, for anoth
Electronics Forum | Tue Feb 19 15:59:55 EST 2002 | pjc
Surface tension is a likely cause. Surface tension is a negative wetting force. You may have a solderability problem. Be sure your flux is properly activated according to the flux mfg. top side board temp. specification. When surfaces to be soldered,
Electronics Forum | Fri Mar 17 21:44:14 EST 2000 | sosina_outry
Daren: suggestion from a friend of mine 1. Is residue on the top or bottom of the board? If on the bottom, then you might need to do solder dedross. if on the top, you might need to check 1. after spray flux, check for any excess flux on the top of
Electronics Forum | Mon Jan 26 11:46:16 EST 1998 | Rin Or
| I have a problem! The solder on my pc boards look great comeing out | of my reflow oven. They go thrue the rest of the prossese | and at the end at the qc station it's cold or whitish or gray not shiny. | does any one have a idea on how to correct
Electronics Forum | Mon Feb 28 16:04:30 EST 2005 | Alex
I use to have that kind of problems with other type of machines and here are the causes: 1- Spray fluxer head partially obstructed (check flow rate) 2- Defective pre-heater probe (manually check temps) 3- PROFILE (last preheat to 280) 4- we sometimes
Electronics Forum | Wed Jun 23 13:34:29 EDT 2004 | df_indy
I am four weeks into my new job, there always seems to be some issues here with PCB every week. Today while I was checking some assemblies with micro-scope, I found a lot of tiny bubbles/blisters on the board. They are just little dots if you look
Electronics Forum | Thu Mar 30 11:07:41 EST 2000 | Wolfgang Busko
> the dirty patch appear seems to be a bit powdery on top of stickiness > the "harden" dirt in the solder pot or at pump are ususally "knock" out while cleaning.. is that thorough enough..? Assuming that 1) is true it might not be thorough enough. On