Electronics Forum | Tue Jun 04 10:39:45 EDT 2002 | jasonfang
Does anyone knows root cause of solderball after reflow? Thanks
Electronics Forum | Tue Jun 04 10:39:54 EDT 2002 | jasonfang
Does anyone knows root cause of solderball after reflow? Thanks
Electronics Forum | Wed Apr 30 18:38:22 EDT 2003 | Guillermo
Yes, I am sorry I forgot to mention that It's inspection after reflow.
Electronics Forum | Tue Apr 13 21:32:42 EDT 2004 | aqueous
Dreamy, OA fluxes / pastes have differing levels of activity. Most OA fluxes must be cleaned very soon after reflow. OA fluxes and pastes, while offering an aggressive flux package and a relatively easy removal (solubility in water), they are the
Electronics Forum | Thu Aug 05 13:50:42 EDT 2004 | mdm4ua
Unless the machine rotates component after vision.
Electronics Forum | Tue Aug 31 13:05:08 EDT 2004 | GS
Indy, could you give me pls, the address of Chemtronics? Tnks
Electronics Forum | Tue Nov 30 11:52:05 EST 2004 | vzsolt
I agree with jdengler. It is very hard if you never done before and for sure will not work 100% after.
Electronics Forum | Fri Mar 03 00:00:17 EST 2006 | John
Mydata sells clips you put on the cover tape after it is removed from the agilis feeder.
Electronics Forum | Mon Feb 21 14:09:24 EST 2005 | JB
Is it before or after reflow?
Electronics Forum | Mon Jul 18 09:35:42 EDT 2005 | stepheniii
If it were other machines I would suggest the possibility of air kiss blowing the solder away, but mydata's have a release to make sure the air kiss never gets too high. Unless it is not pointing 90 degrees away from the machine like mydata recommend