Electronics Forum | Tue Mar 06 17:24:31 EST 2012 | acsscott
OK, did some more testing this afternoon. First, I moved the LED’s from feeder location #23 to Feeder location 30. This is three down from the other component(#33) it is picking, so it should be able to hit them both at the same time for two of the
Electronics Forum | Thu May 17 11:39:38 EDT 2012 | stentech
Hi again quickly. Anyone need a sample let me know ..no charge. I would be evry interested in your findings and can give many references for you to talk to..customers. Scott I am working on a project with different cut parameters very time consuming
Electronics Forum | Wed Jul 03 09:13:23 EDT 2013 | dontfeedphils
I currently run the HLC software suite with a 750/760 line and another 2060 line. For the 750/760 line I have to stick with the older HLC, version 4.5 I believe, which I actually run inside of a Windows 98 virtual PC using a dongle emulator. The 20
Electronics Forum | Tue Jul 30 15:04:54 EDT 2013 | ericrr
Is it just possible that H49s crysats are hard to place, so it looks like it has been place by a perfectionistic instead of looked like it had a parachute type loading. This is the H49 short stubby type crystal about 10 mm long (width) about 4.5 mm
Electronics Forum | Thu Dec 08 13:34:46 EST 2016 | spitkis2
We are currently experiencing with our SMD Solder > Reflow Equipment on Shooting-Up Zones (Zones > 3,4,5,7 & even Cooling Zone). PV exceeds about > 5-10 degrees with the SP. (ex: SP=140deg, actual > PV = 145deg & higher). Our equipment undergo a
Electronics Forum | Mon Jun 07 12:22:44 EDT 1999 | Chrys Shea
| I'm encountering a new problem at my new company that I haven't encountered before in my past life - and that's Wave Soldering VIA holes. | | We've been getting a rash of defects that we call in this company, "insufficient solder in VIA hole." The
Electronics Forum | Mon May 20 21:29:52 EDT 2002 | davef
Q1: Are we saying then that IMC can occur at the solder / Cu pad join on the PCB when finished assembled? A1: Yes, but in a broader context I am saying that when someone solders correctly, they form an IMC. Q2: Will the tin diffuse with the Cu over
Electronics Forum | Thu Apr 22 08:43:25 EDT 1999 | Michael N.
| | I'm having problems with trying to get a good solder joint using a Ceramic PCB. We are using AMTECH hi-temp solder (ws-486 96.5/3.5ag). My profile looks great and I used the recommended profile from Amtech with a few adjustments. My max temp is a
Electronics Forum | Mon Nov 09 09:44:22 EST 2015 | davef
Purpose. This describes setting-up a wave soldering system set-up for a new assembly design or checking a wave solder machine operation with a test board. Applicability. To be used for new design printed circuit assembles and during machine accept
Electronics Forum | Thu Apr 03 22:56:48 EDT 2008 | davef
Potential impacts of using expired solder paste are [University of Bolton]: * Changed paste rheology. Result: poor print quality * Loss of solvents. Result: reduced flux activity * Changed flux formulation. Result: More difficult to clean flux residu
winsouce.jpg)