Electronics Forum | Thu Dec 14 10:14:04 EST 2000 | PeteB
Jacqueline, Asuming you mean immersion silver: Advantages - Very flat finish compared to HASL, more easily solderable than bare copper with OSP and more process tolerant than this in our experience, reasonable shelf life, cheaper than immersion gol
Electronics Forum | Wed Oct 06 04:11:35 EDT 2010 | grahamcooper22
I've done minimal research to this point and > understand my issue with solder on the double > sided boards is due to oxidation that occures on > the unpopulated pads when the board makes its > first trip through the reflow oven. > > We did run
Electronics Forum | Thu Jan 25 04:55:08 EST 2007 | greg york
Strange as we have had huge problems with Silver in Many different Assembly houses. Mainly with Nitric Acid based Silvers causing blow holes, non wetting and even the Nitric etching away the tracks on fine boards. It has been one of the main problem
Electronics Forum | Tue Aug 24 14:49:58 EDT 2004 | jamyboy
Hi, I am trying to assemble a LTCC component > with Pd/Ag surface finish on to Sn/Pb/Ag solder > and Sn/Ag/Cu solder. I am passing it through a > reflow. I have observed poor wettability at the > solder-pad joint. Does anyone have information
Electronics Forum | Wed Sep 19 14:23:31 EDT 2001 | jschake
Pad Metallurgy Used: Copper OSP pads were used for all of the results that I have been reporting. The same design test boards with Nickel/Gold pads are available and awaiting further assembly tests. I will consult with a board technology and metall
Electronics Forum | Mon Nov 19 20:15:39 EST 2001 | davef
Now, that is one thickass board!!! The rant first: If our �board supplier changed our board surface finish on� anything without our approval, the board supplier would be an �X�. Life has enough surprises. And of all the flat finishes available, h
Electronics Forum | Mon Feb 09 08:34:50 EST 2015 | saoasasd
In my case most of the PCBs are OSP finishing and worst case of MSD component on bottom side is level 3 (168 hours). You mean that PCB shelf life with bottom side assembled shoud be 84 hours?
Electronics Forum | Thu Sep 02 10:00:29 EDT 2004 | russ
If you are concerned about shelf life and handling of raw or partially assembled PCBs use Immersion gold and hope that you don't get black pad, I still love this finish but I have been fortunate to never receive bad boards. If I understand your ques
Electronics Forum | Wed Jul 19 14:53:39 EDT 2006 | amol_kane
i think the most important thing to consider is the # of reflows. is this a double sided assembly? if so OSP degrades during the first LF reflow. also there are many studies out there that show the wetting on OSP is inferior to some of the other comm
Electronics Forum | Wed Jan 13 15:47:57 EST 2016 | dyoungquist
What surface finish are you using on the bare PCBs? ENIG, Silver, OSP, Leadfree HASL, etc.?