Electronics Forum | Wed Oct 19 20:04:06 EDT 2011 | warwolf
yeah I’ve tried to go down the road of internal recycling but the company carnt justify spending 20k on a machine that does it. Ah but where still onto it in other places though our SMT department has very minimal wastage on solder paste as we have b
Electronics Forum | Thu May 15 21:52:33 EDT 2008 | deni
Can anyone tell me what makes the wave solder machine lead free? I I am looking to buy a used machine "electrovert minipak 300" and they are claiming that they can convert the machine into lead free. I want to know what does involve to do this kind o
Electronics Forum | Wed Oct 07 15:44:43 EDT 1998 | CW
There's a good article on lead-free assembly of mixed technology in the May issue of SMT Magazine (pg. 52)
Electronics Forum | Wed Mar 05 11:53:34 EST 2003 | davide grosso
I want to know the advantage of using complete inert soldering wave machine (with Nitrogen, Tunnel concept) in comparison to use just a soldering machine withe inerted solder pot. Thanks
Electronics Forum | Wed Oct 19 11:33:15 EDT 2011 | caerleon
easier if you recycled on-site? You can still send off for reclaimation the oxide powder that your left at the end of the process. Failing that talk to your supplier to see if they have arrangements to do this for you or look at reducing dross - i f
Electronics Forum | Sat May 17 09:12:50 EDT 2008 | davef
Lead-free means expensive tin. Tin is an excellent solvent. So, metal parts in contact with molten tin must be expensive enough to resist that nature of tin. To learn more about this: * Search the fine SMTnet Archives * Look here: "Liquid Tin Corrosi
Electronics Forum | Thu Nov 03 09:43:55 EST 2005 | lupo
Check flux penetration and type of flux. How much is solid contents. The solder filling is better under Nitrogen. Check the time (speed) of the nozzle whether is correct. Usually For SAC305 the temperature of bath is 320C/degrees, but only for sel
Electronics Forum | Thu Apr 15 11:13:24 EDT 2004 | pjc
Sn corrosion effects were studied for stainless steels, coated stainless steels, titanium, cast iron, and other materials. This study can be found in the SMT Library under "Equipment Impacts of Lead-Free Soldering" Electrovert uses a Melonite coating
Electronics Forum | Fri Aug 12 13:17:00 EDT 2005 | patrickbruneel
To all smt neters, In many different threads I have tried to bring awareness of the dangers lead free alloys pose to the reliability of solder connections. Many times those warnings have been waved by unscientific reports (from lead free solder manu
Electronics Forum | Wed Nov 02 11:14:45 EST 2005 | Doug
I am doing lead free testing on a Vitronics selective machine with a 4 mm nozzle. The finishes I am testing are ENIG, ImSn, and ImAg. The problem I am encountering is achieving good top side wetting. Has anyone had any luck with this type of an ap
Main Products: 1. Original new and Original Used SMT/AI Spare Parts. 2. SMT Equipments And Related Machine( SMT Calibration, SMT Feeder Carts,Conveyer etc.) 3. Maintenace and Repair Service Pre-Sales Service Provide details ab
Manufacturer's Representative / Manufacturer / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
3 Road Xintang， Fuhai Street，Fuyong
Shenzhen, 30 China
Phone: 13713862102