Electronics Forum | Mon Jan 29 12:42:24 EST 2001 | davef
Several points about your query are: * TI�s solderability protection specification is a minimum of 3 u" of palladium over 40-60 u" of nickel plate over a http://www.ti.com/sc/docs/products/logic/package/palladm/index.htm
Electronics Forum | Mon Jan 29 06:44:59 EST 2001 | Scott B
I have recently come across a device which has a palladium over nickel finish which when soldered shows evidence of poor wetting to the lead ( i.e. a wetting angle greater than 90�) about three quarters of the way up the side of lead. This is only vi
Electronics Forum | Thu Jul 15 06:27:50 EDT 2010 | xps
Hi after an enviromental test 85C/85RH, for 3 months (powered), of an electronic assembly with edge finger tabs ENIG finished (nickel 5micron, gold 0.02micron), the nickel disappears completely under the gold (due to corrosion, I think). Does anyone
Electronics Forum | Thu Jul 15 13:27:42 EDT 2010 | xps
Thanks... anyway I confirm, the nickel disappear (verified by cross section)and a strange substance greyish above gold, covering the tabs after test. I don't know the reason for this phenomenon. I don't believe that with proper electrolytic nickel fi
Electronics Forum | Thu Mar 31 17:27:36 EST 2005 | russ
Are we possibly talking palladium instead of platinum? I haven't yet heard of platinum terminations (seems expensive) If it is palladium over nickel, I can tell you that you need to reach 225-230 Deg. C in reflow and the TAL should be about 90 sec.
Electronics Forum | Thu Mar 31 19:52:50 EST 2005 | davef
We agree with Russ that you're talking palladium instead of platinum. Your wetting problem likely is not the Pd-Ag surface layers, but the underlying metal or nickel to which you need to wet. Either a base metal is: * Contaminated and poorly wettabl
Electronics Forum | Tue Nov 29 21:51:37 EST 2005 | wmeyers
I have a pin and sleeve assembly that utilizes a fusible link type of solder, Bi, Cd, Pb and Sn alloy. The pin is gold plated, the sleeve is copper alloy 725. I have had sporadic success with wetting of the sleeve during the reflow process. To improv
Electronics Forum | Mon Apr 28 09:59:04 EDT 2003 | davef
Your customer's question is reasonable. Soldering to nickel is not always a walk on the beach [can of corn, or whatever]. This issue is flux not solder. Your Sn63 will have plenty of strength, providing the solder connection is well formed. You s
Electronics Forum | Wed May 11 13:27:30 EDT 2005 | Sam Ho
i want to know which type of solder paste and reflow profile can support the solder pad with nickel but not covered gold on the pcb.
Electronics Forum | Mon Oct 27 20:01:00 EDT 2014 | rangarajd
Hello, We are facing solderability issues on a particular lot of board. THe Nickel thickness measured with an XRF is around 400 U inches. Spec calls out for 130 u inches Nickel and 3 - 5 U inches gold over it. Assuming there is no porosity on the g