Electronics Forum | Thu Aug 13 16:25:11 EDT 2015 | emeto
Loctite 3609. Just a small dot under the D-Pak and it works 100%.
Electronics Forum | Tue Aug 11 09:48:22 EDT 2015 | samputrah
We have had two jobs that have the same issues with DPAK's sliding off their pads during reflow. We tried to resolve this by placing epoxy on the side of the component to create a "dam". However this is not repeatable enough to be a quality resolutio
Electronics Forum | Tue Aug 11 09:52:53 EDT 2015 | rgduval
I assume that these parts are falling off during second-side reflow? The easy solution, of course, is to not build high-mass components on first-side reflow. If this isn't practical, however, you can try using epoxy/glue under the component. We'
Electronics Forum | Thu Aug 13 14:10:01 EDT 2015 | markhoch
Hi Sam, I have a feeling that what you're trying to communicate is that your DPAK's are skewing off the pad during reflow. This is caused by a thermal "mismatch" where the solder paste on one side of the DPAK becomes molten before the other, then th
Electronics Forum | Fri Sep 14 01:43:36 EDT 2001 | dhanashekar
please check the following also. in one of the cases we came across the second point was the problem. 1. the parallelisum of the conveyor. 2. the warpage of the board. 3. the stencil.(the differential height in the paste deposition of the two pads
Electronics Forum | Fri Sep 28 09:30:07 EDT 2001 | kmorris
Just had a similar phenomenon 2 days ago. May relate to your issue --- or not. Like you, I did a once over looking for mechanical obstruction & couldn't find any. Ran a thermal profile on the offending PCB & all checked out. Looked in end of oven
Electronics Forum | Wed Jul 01 04:54:28 EDT 2015 | jvercamm
hi, the last post on pad cratering dates from 2012. We have (likely similar) problems with a RoHS 783 solder ball BGA size 29x29mm^2 (organic package BT), pitch is 1mm and solder ball diam is 0.5mm the field failure is after 12 months, almost exclu
Electronics Forum | Mon Jan 24 06:19:04 EST 2011 | fönsi
Hello! I've had the same problem about one Jear ago. We had exessive building of voids in the solder joints. I recomment to take a pincer to break off some of the components. If the solder joint is good, the copper pad will stay at the solder joint
Electronics Forum | Thu Feb 14 08:14:12 EST 2008 | davef
Questions are: * Do the BGA pads on the board take solder when you solder them by hand? * What is the temperature on the BGA pads during reflow? * What is the temperature on the other component pads during reflow?
Electronics Forum | Thu Sep 13 11:21:45 EDT 2001 | aldo_maldonado
We've had several instances of parts (1206R, SOT-23) popping off of their location during reflow. Parts placement is OK, paste brick is aligned and compact before oven. But we get random parts off their location just lying somewhere else on the boar