Electronics Forum | Tue Jun 14 18:32:44 EDT 2005 | GS
Hi Peter, which should be the best cooling rate once belove TAL by using L-F alloy ie. SAC 305 ? Tnks GS
Electronics Forum | Tue Feb 01 09:21:36 EST 2005 | TomA
I looked breafly at this alloy. My concern was that I had already implemented a SAC 305 alloy at SMT. So any of my mixed technology projects would one alloy (SAC 305) on one side (topside) and a different alloy (SN100C) on the bottomside. Most articl
Electronics Forum | Mon Jun 20 21:54:38 EDT 2005 | darby
Contact your paste supplier and see what they say. My information on SAC 305 FROM MY SUPPLIER was - "The cool down rate is not as critical for Pb-free solder joints, as it was for SnPb. The grain sizes do not differ is size in the Pb-free bulk solde
Electronics Forum | Tue Apr 05 15:32:49 EDT 2011 | grahamcooper22
It is one of our pastes...Almit LFM48 W TM-HP, a high reliability no clean solder paste based on SAC305 with a size 4 powder. It's a paste that works so well we have thousands of users of it worldwide. Why are you using SN100C alloy paste ? I imagin
Electronics Forum | Fri Sep 07 12:19:20 EDT 2007 | guqing
We are having problem to develop lead-free (SAC305) reflow profile for big SMT electrolytic caps. The delta T of the joint of the cap with the rest of the board is too big to fit in the tighter lead-free window. Any suggestions regarding the total pr
Electronics Forum | Thu Jan 20 17:14:39 EST 2005 | jbrower
Today, I have just finished evaluating Kester's EM907 (SAC305)lead free solder paste and found that for our applications it performs as expected. End result that I am encouraged with the results that we got. The equipment that I used: An SMT2020 to
Electronics Forum | Mon Jan 23 19:48:27 EST 2012 | gaz
This make me curious how many people are using sn100 versus how many using sac305. The sn100 seemed to generally cover the pads and flow a little better, and looked nicer, but SAC305 overall was easier. Is this normal or do I need to work more on sa
Electronics Forum | Thu May 29 13:12:10 EDT 2008 | yam6rider
Just like to know what you guys thoughts regarding mixed alloys. Production run SAC305 and some components are SAC105. So, which profile should you follow. SAC105? or SAC305.
Electronics Forum | Thu Sep 05 11:05:35 EDT 2019 | SMTA-Tony
There are competitors to REL solder alloys from AIM. Tin-Copper-Nickel-Bismuth alloys (Nihon Superior) are an alternative option which do very well in thermal cycle testing. The reflow profiles required are similar to SAC305 profiles. You may als
Electronics Forum | Mon Jul 07 11:46:29 EDT 2008 | aj
Hi All, Can anyone advise the spec for land size of a lead 0.2mm in width? I am placing a TQFP128 0.4mm pitch, the leads seem to be wider than the actual pads they are been placed on? I am also experiencing poor wetting on this part , it has NiPdAU