My specialty. Your right, Most corrugated contains S02 and the pallet is usually out gassing formic acid as well. Not a great environment for silver. Original press release follows: Reactive Polymers At AT&T Bell Labs, John P. Franey has developed
Electronics Forum | Thu Apr 29 18:48:11 EDT 1999 | Kiet Dang
Hi, Did anyone experience a problem with electrically conductive silver filled epoxy is resistive due to galvanic reaction? I'm having this problem when attaching components to Ni plated housing while conducting an experiment to cost reduction for Au
Electronics Forum | Thu Aug 12 20:32:44 EDT 2004 | usdigital
Indy, We use Palladium silver surface finish parts for silver epoxy attached parts only. It is our understanding that this finish is not for solder, but only silver epoxy attach. I expect that is you problem. Dave
Electronics Forum | Thu Jun 08 09:43:42 EDT 2017 | davef
You know the scary part about your mentioning a tread where I post something? Well. let's just say that 2007 was a long time ago. Anyhow, silver will dissolve into your solder and provide no barrier. Some people apply a silver flash plating over the
Electronics Forum | Thu Jun 08 16:12:19 EDT 2017 | davef
Your plater's recommendation should work fine. Your simple copper plate will work, but you'll be stepping into fighting a copper tarnish battle. Silver over the copper is a better choice. I was thinking a silver thickness of a minimum of 3 microns
Electronics Forum | Tue Jan 20 11:54:12 EST 2009 | smt_guy
Is this Corrosion? We found our boards with this issue 45 days after they were delivered to us from supplier. The board finish is HAL Leaded. But I noticed that the corrosion like issues are coming form the tiny via holes with SILVER EPOXY FILLING.
Electronics Forum | Wed Apr 18 08:14:20 EDT 2007 | davef
Silver palladium termination * AgPd-terminated capacitors are designed for conductive adhesion. Reflow or wave soldering is not recommended. [EPCOS Multilayer ceramic capacitors, Soldering directions, October 2006] * CONDUCTIVE EPOXY BONDING. Epoxy c
Electronics Forum | Thu Sep 17 23:36:35 EDT 2009 | Sean
All, We know that incomplete immersion silver could potentially lead this creeping corrosion. Is there any way to check bare PCB for incomplete immersion silver coverage, especially on the via hole area? Thanks, Sean.
Electronics Forum | Sat Sep 25 07:07:02 EDT 1999 | Brian
| I need a memory jog. What is the term for the growth of conductive contamination after a board is in storage or field? | There are several different mechanisms which can cause this. In reality, ionic contamination is the root cause for many of the
Electronics Forum | Tue Sep 22 08:55:48 EDT 2009 | geb
Hi Chris, We've had another supplier say that it is the silver or combination of tin with silver that causes the corrosion. Would you agree?