Electronics Forum | Wed Jan 11 16:15:11 EST 2006 | Cmiller
What alloy are you using in your wave? SN100, SAC305, SACX?
Electronics Forum | Fri Mar 03 13:44:36 EST 2006 | Jon Provost
We switched to Sn100C on 2 waves and kept one with SAC305. The SAC305 will be converted to SN100C as soon as the Aim rep. delivers it next week.
Electronics Forum | Thu Feb 15 10:48:34 EST 2007 | ck_the_flip
Is there anybody out there doing this scenario: SAC 305 Reflow & SN100C Wave and Selective Can the 2 alloys be mixed on 1 board, say, SAC 305 for SMT, and SN100C for thru-hole? Are 2 different rework chemistries needed, or can one use SN100c wire
Electronics Forum | Thu Apr 06 17:42:59 EDT 2006 | GS
found this interesting comparison (SAC305 SN100C) http://www.nihonsuperior.co.jp/english/data/pdf/nse2_1.pdf Regards..........GS
Electronics Forum | Mon Jan 02 08:54:58 EST 2006 | aj
has anyone used or trialed the SACX from Alpha, from reportes and studies carried out it seems that its a go between SAC305 and SN100.
Electronics Forum | Wed May 03 11:26:57 EDT 2006 | George
Sheldon, Try using SN100C wire solder. It seems to extend the life of the tips plus solder joints look much better. We use both, clean and No-clean. We had the same problem while using SAC305... Thanks, George
Electronics Forum | Fri May 19 13:40:36 EDT 2006 | grantp
Hi, Sorry to drag this thread up again, but we were recommended to change the wave to SAC305, but is everyone recommending SN100C? That seems to be the feeling on this thread. What flux is used? Regards, Grant
Electronics Forum | Fri Mar 03 14:43:04 EST 2006 | amol_kane
the latest circuits assembly mazagine features an article on this by Karl Seelig
Electronics Forum | Thu Apr 06 18:22:53 EDT 2006 | russ
Anyone using the new SACX from Alpha?
Electronics Forum | Fri May 05 09:00:46 EDT 2006 | russ
Studies showed that there are no issues mixing SN100C and SAC305, I believe that AIM has this info. Russ