Electronics Forum | Wed Dec 08 12:48:01 EST 1999 | Chuck C.
Is anyone out there having problems with noise in analog circuits caused by the residue that no-clean solder paste leaves after reflow? If so do you have any suggestions on how to eliminate the problem??
Electronics Forum | Tue Mar 20 09:31:56 EST 2001 | PeteC
I dunno.: e�lec�tro�lyt�ic Of or relating to electrolysis. Produced by electrolysis. Of or relating to electrolytes. e�lec�trol�y�sis Chemical change, especially decomposition, produced in an electrolyte by an electric current. Destruction
Electronics Forum | Wed Oct 23 14:33:44 EDT 2002 | lhoang
Any one encountered the problem such as poor conductivity when the silkscreen mis-registrated on the solder pads ? Thanks; Linh
Electronics Forum | Sun Nov 03 08:28:29 EST 2002 | davef
We have had poor solderability from silk screen being on pads, but have never measured the conductivity.
Electronics Forum | Wed Jul 27 09:47:01 EDT 2005 | GCampbell
CEMCO Uk have done testing using SACX0307, SAC305 and Sn/Cu/Ni. The copper dissolution tests (report available) conducted at CEMCO showed that the lowest copper erosion rate was achieved by SACX0307. Regards Gerry
Electronics Forum | Thu May 11 11:25:56 EDT 2017 | davef
Key to Rosin Fluxes [from SUPERIOR FLUX & MFG. CO.] Type R (Rosin): Non-activated rosin flux for soldering copper. Residues are non-corrosive and non-conductive. Type RMA (Rosin Mildly Activated): Mildly activated rosin flux that contains no chlori
Electronics Forum | Thu Apr 17 10:38:02 EDT 2003 | davef
While Russ is correct that a little voiding is OK, your level of voiding [customer complains that the solder surface looks bumpy] doesn't give us the ol' warm and fuzzy about their process control. For background: * Search the fine SMTnet Archives.
Electronics Forum | Thu Jul 17 20:20:12 EDT 2008 | davef
Wave set-up DOE * Immersion depth [1/3 to 2/3 of board thickness] has the least impact of any variable in wave soldering. * Contact length the greatest impact. * Control flux density, time through preheaters, top side temperature as the board reaches
Electronics Forum | Thu Mar 22 16:35:06 EST 2001 | Steve
Deja vu! When I read your response I turned around to see if you standing behind me listening to our problem. We currently make about 50 different boards all using no-clean that have no problems, yet this newest boards has a couple of issues that eng
Electronics Forum | Tue Dec 17 16:27:02 EST 2002 | davef
I�m not clear on the problem. What I get: * Your fabricator did not deliver the product that you asked for in your purchase order. * Pad. Land. A portion of a conductive pattern used as a termination area. Metal surrounding a hole on a printed ci