Electronics Forum | Tue Feb 15 00:27:39 EST 2011 | jeffr
First clean and de-bur the hole in the nozzle, then try it again. If the Head does not pick up at the feeder, then moves to the dump position...it means that the Vacuum Sensor Board has detected that the nozzle vacuum is above the LOW threshold setti
Electronics Forum | Wed Feb 16 01:06:13 EST 2011 | vinitverma
Dear Gabe, Once you have the mount data in the program, you can move the camera automatically to the location by tracing each location one by one. If I remember it correctly it is done by having the location highlighted in the program and then by pr
Electronics Forum | Thu Feb 17 09:35:16 EST 2011 | ravo
Hi everybody, I am here seeking your experience and asking your help, I want to update our SMT production line as I already hace FUJI CP6 and QP242 machines beside GL2 and oven our new product including 60 components 0402 (1mm*0.5mm ) and 2 BGAs w
Electronics Forum | Thu Feb 17 18:15:57 EST 2011 | rodrigo
Hi All, Does the Inspector software have a library manager? I see a "Standard" and an "Alternate" library folders. The standard library shows the outline (like a footprint) for the components but the alternate library has pictures and outlines with
Electronics Forum | Wed Feb 23 00:45:49 EST 2011 | tsvetan
Does someone with technical knowledge knows what exactly happend with the solder paste after the shelf life pass? What we have seen is sometimes flux separation which disapear after a good mix, and change of viscosity i.e. drying. The tin, silver and
Electronics Forum | Wed Feb 23 03:12:25 EST 2011 | pkannan
You are very right. There are 2 major factors 1) There is going to be Flux separation. This is basically due to fact that metal particles are heavier than the Flux vehicle system, and due to gravity effect they slowly drift downwards leaving the ligh
Electronics Forum | Wed Feb 23 03:22:47 EST 2011 | pkannan
(Corrected the Subject line - sorry for Spelling ) You are very right. There are 2 major factors 1) There is going to be Flux separation. This is basically due to fact that metal particles are heavier than the Flux vehicle system, and due to gravity
Electronics Forum | Thu Feb 24 22:32:56 EST 2011 | rstadem
PKannan, Your opinion is contrary to J-STD-005 "Requirements for Soldering Paste". Within that document is included specific requirements for re-certification of expired solder paste. Paste that is expired can be used after a simple viscosity test an
Electronics Forum | Sat Feb 19 11:40:40 EST 2011 | ravo
Hi everybody, I am here seeking your experience and asking your help, I want to update our SMT production line as I already hace FUJI CP6 and QP242 machines beside GL2 and oven our new product including 60 components 0402 (1mm*0.5mm ) and 2 BGAs w
Electronics Forum | Thu Feb 24 12:40:29 EST 2011 | thenrz
Hello all! Here's my issue: I've been assigned to make a programming fixture for a contract product we've been making. We're ramping up to 300+/month so it's becoming necessary to have more permanent fixtures. Usually, when programming, we have a