Electronics Forum | Thu May 28 08:39:13 EDT 1998 | Rob Williams

I have a component that is glue cured on the bottom of a pcb. The component is a 1206 size jumper. It is made up of iron/nickel alloy. The problem I am having is that the part will fall off the board during wave solder. Is the component not able

1206 Jumper

Electronics Forum | Thu May 28 08:38:43 EDT 1998 | Rob Williams

I have a component that is glue cured on the bottom of a pcb. The component is a 1206 size jumper. It is made up of iron/nickel alloy. The problem I am having is that the part will fall off the board during wave solder. Is the component not able

1206 Thickness

Electronics Forum | Thu Oct 18 12:58:07 EDT 2001 | jacob

Hello, We recently changed a component on one of our products from a .5% 1206 resistor to a .1% resistor. I noticed that there was a greater rejection rate of the .1% resistor during placement. Apparently the thickness of the .1% resistor is less th

1206 Thickness

Electronics Forum | Thu Oct 18 18:57:35 EDT 2001 | davef

I doubt that it has as much to do with the tolerance as it does: * Who manufactured the part. * What technology was used in fabricating the part. We get various thickness for the same part number [ie, pakage size, value, power, tolerance, etc.]. It

Ferrite Bead 1206

Electronics Forum | Sun Oct 31 19:34:43 EST 1999 | Pat Copeland

I am currently placing aprox. 95 to 100 1206 size ferrite beads onto a pcb and having difficulty solding these parts. They appear to be soldered when the board comes off the reflow, but you can flic the parts off by hand. We thought they were contami

Re: 1206 Jumper

Electronics Forum | Thu May 28 09:48:08 EDT 1998 | Steve Herring

I have a component that is glue cured on the bottom of a pcb. The component is a 1206 size jumper. It is made up of iron/nickel alloy. The problem I am having is that the part will fall off the board during wave solder. Is the component not abl

Re: Ferrite Bead 1206

Electronics Forum | Tue Nov 02 11:16:45 EST 1999 | Dave F

Pat: No, but if you describe the situation we may be able to sort through your soldering problem. Good luck. Dave F

Re: 1206 Jumper

Electronics Forum | Wed Jun 03 09:48:47 EDT 1998 | Gary

I have a component that is glue cured on the bottom of a pcb. The component is a 1206 size jumper. It is made up of iron/nickel alloy. The problem I am having is that the part will fall off the board during wave solder. Is the component not abl

Re: 1206 Jumper

Electronics Forum | Thu May 28 22:49:32 EDT 1998 | D. Lange

I have a component that is glue cured on the bottom of a pcb. The component is a 1206 size jumper. It is made up of iron/nickel alloy. The problem I am having is that the part will fall off the board during wave solder. Is the component not abl

Re: 1206 Jumper

Electronics Forum | Thu May 28 08:56:12 EDT 1998 | Earl Moon

I have a component that is glue cured on the bottom of a pcb. The component is a 1206 size jumper. It is made up of iron/nickel alloy. The problem I am having is that the part will fall off the board during wave solder. Is the component not abl