Electronics Forum | Wed May 09 15:15:52 EDT 2001 | caldon
Your process needs some refining. How long did it take to wet? How much force did it take to break the surface tension? What type of solder was in the solder pot? What type of flux was used? What was the pot temperature? Did you take a cap and p
Electronics Forum | Thu May 10 10:27:29 EDT 2001 | davef
It depends ... * Components stored in a garage in Chiriqui,Panama will have a different shelf life than those store in a climate controlled room in Ayrshire, Scotland. * Components from a reputable supplier will likely have a different shelf life tha
Electronics Forum | Thu Jan 09 15:40:58 EST 2014 | davef
Batch cleaner Aqueous Technologies, 9055 Rancho Park Ct, Rancho Cucamonga, CA 91730; 909-944-7771 F909-944-7775 aqueoustech.com Austin American Technology; 12201 Technology Blvd, Austin, TX 78727; 512-35-6400 F512-335-5753 aat-corp.com EMC Global Tec
Electronics Forum | Wed Sep 08 11:26:08 EDT 2021 | kumarb
Use a free cloud service like udrop or wetransfer. From your description, the plating is coming off the pogo pin itself ? Also, unless you absolutely cannot sub the part, consider the following vendor - have others as well that service the 'pogo p
Electronics Forum | Mon May 15 19:55:31 EDT 2000 | Dave F
Greg: The best one is the cheapest used one (that fits in the hole) from any company whose name you recognize, like: Simplimatic Engineering, POBox11709 Lynchburg VA 24506 800.238.3700 fax804.582.1200 Pat Ortz 561.793.9140 fax407.793.9568 Process C
Electronics Forum | Wed May 09 13:11:22 EDT 2001 | zam_bri
Hi.. Recently, I have received a few reels of 0402 with an old date code ( but still less than 2 years old).I don't have a capability in-house to carry out the solderability test except for the dipping test ( dip the components in the molten solder
Electronics Forum | Wed May 09 17:26:57 EDT 2001 | davef
Awww, don beso tuff on ursef!!! It sounds like you�re thinking correctly with what you�ve done, but it�s possible that the test you ran did not represent your actual production environment as well as you would have liked. So, you just need to "cran
Electronics Forum | Thu May 10 09:57:22 EDT 2001 | zam_bri
Hi Cal/Dave F, Good news today. The problem went away when I received and ran with a brand new component today. But I'm sure with a robust profile, I should be able to compensate oxidations at some degrees, rite? ( taking into consideration the suc
Electronics Forum | Mon May 24 04:01:10 EDT 1999 | Joe Manzur
John, We are using a well known solder paste, begining with the letter "H". (I don't want to be accused of advertising). Also, we are now using a board inverter. In the early day's however, before we purchased a board inverter, we were having to