Electronics Forum | Wed Jul 31 07:51:31 EDT 2019 | ameenullakhan
Hi Dave, lead is 80Pb/20Sn. Top joint off CCGA lead is SN63/Pb37. Thermocouple was placed at center lead of the CCGA and one at the corner lead of CCGA. Ramp Rate Center 1.09 Corner 1.26 Soak ( 140 - 160 deg C ) Center 37sec Corner 38sec Ref
Electronics Forum | Tue Nov 12 09:04:21 EST 2019 | mario85
Hello Guys, I'm new here. I am smt process engineer in new company located in Poland. I am responsible for whole smt line, so I have a lot of problems at the beginning :). I would like to ask about few things. The topic is solder balls. I produced s
Electronics Forum | Wed Oct 19 07:04:06 EDT 2022 | winston_one
If any changes in design is not possible and you have to solder it, it's a real headache, I know... I see only 3 options here that you can try consiquently: 1) Accurately profile the board and optimize a profile (go to lower limit of process windo
Electronics Forum | Tue May 25 10:56:12 EDT 1999 | John Thorup
| | | Can anyone steer me towards a supplier of heatsinks suitable for use on a PQFP 160. Before you shoot me down in flames, I know that I am not going to get much heat away from the die because of the plastic but the application is such that the bo
Electronics Forum | Tue Jul 28 02:28:48 EDT 1998 | Bob Willis
The causes for solder on gold are: Paste wash offs Dirty stencils Dirty under stencil cleaning cloths/no solvent Poor handling The most common reason is wash offs when there is a couple of balls left on the tabs and they reflow. With correct profile
Electronics Forum | Fri Dec 08 21:26:44 EST 2006 | billwestiet
You already have some good answers. A chemical isolation zone for RMA is a good idea. If you are looking for new see the two references you have and Austin America. If you are looking for used, see us at http://www.ietechnology.net. We presently
Electronics Forum | Thu Feb 10 10:28:56 EST 2000 | Russ
Okay, Okay, here is the rest of the story! These boards were definitely plated, reworked to HASL, The component that is the most succeptable is a 160 pin QFP .5mm pitch. This component has nickel/iron lead frame. Significantly reduced apertures (1
Electronics Forum | Tue Oct 31 14:52:25 EST 2000 | Dr. Kantesh Doss
Hi Antonio: You clearly have printed excessive amount of solder paste on the pad. You can reduce the amount of paste by one or two methods: 1. Switchover to 5 mil thick stencils. 2. Change the design of your stencil openings (at the discrete compone
Electronics Forum | Thu Jul 20 16:10:34 EDT 2000 | armintan
Hi Bob, From my memory about almost 4 yrs. ago, I remember we did something similar to this in Apple Computer Singapore. Process sequence are: Bottom Side Process: Print Solder Paste(Dek 265GS) Dispence Adhesive (Cam/Alot 3800) Place Components (
Electronics Forum | Thu Dec 16 16:46:47 EST 1999 | Mike Naddra
Steve , I use a general set of guidlines when developing reflow profiles: Ramp rate to 140 deg C - 50-60 seconds Time at preheat (140-160 deg C) - 90-120 sec Time above liquidous (183 deg C) - 45-90 sec Time at peak (215-225 deg C) - 9-12 sec peak t