Electronics Forum | Mon Aug 17 02:57:47 EDT 1998 | Bob Willis
| | Looking for Suppliers of surface mount wetting balance equipment. | Bucky: Section 6 of the ANSI/J-STD-002 specification lists wetting balance suppliers. Dave F I like and continue to use the Multicore system. I have had many ours using the sys
Electronics Forum | Mon Feb 14 12:07:47 EST 2000 | Dave F
Leslie: Product screens and tests of prototypes and test vehicles should be tailored for the specific goal and product. I caution your use of equations and test condition information without specific use environments and design conditions. Lawyer:
Electronics Forum | Wed Jan 17 20:48:14 EST 2001 | davef
We find that the raw BGA's pad sheared surface has the SnPb solder at various Z heights whereas the assembled BGAs pad leave a smooth layer of SnPb along the pad. Like to understand the cause for the difference. Who could guess? Solder joint streng
Electronics Forum | Thu Oct 12 22:16:59 EDT 2000 | Dreamsniper
Hi Guys, I'd like to share this to all of you...you can start playing with the rests...Stated prices, if not indicated, are in Aussie $ or Singapore $. Stencil Printing Adhesive Pros a) Less Capital Equipment Cost (Short Term). In reality it is f
Electronics Forum | Tue May 08 11:27:49 EDT 2001 | Eyal Duzy
I will review some of the advantages/disadvantages of AOI vs. X-Ray one by one according to the main differences that you may find between them. * AOI uses optics that can "see" only visible elements. X-Ray can "see" hidden elements. There is a ve
Electronics Forum | Mon Jan 31 12:24:24 EST 2000 | Dave F
Robert: Several points: 1 Dross is a mixture of various things with no "fixed" composition: � The obvious things are metal oxides mixed with metal and this can vary in color with temperature and composition - remember some intermetallic oxides form
Electronics Forum | Fri Jan 21 14:51:08 EST 2000 | Dave F
Mike: I�d hate to see you making design decisions, based solely on the discussion here, but that this would be an impetus to consult IPC-D-279, "Design Guidelines ... " and take a course on designing reliable boards. Werner Engelmaier (Engelmaier
Electronics Forum | Wed Nov 17 11:20:23 EST 1999 | Dave F
Hey Gyver: If you don�t mind (which you don�t have any choice about, because I�m going to do it anyhow, cause it�s MY word processor), I�m going to respond genericly, but still be directed to your question. Much of the following is paraphrased from
Electronics Forum | Mon Oct 11 11:13:32 EDT 1999 | Wirat S.
| | | We've recently encountered this problem where one of our .050" pitch BGA's were reflowing at the wave thus causing shorts... The board was profiled with probes stuck to a QFP solder joint, an 0603, and one of the BGA joints. There was an almo
Electronics Forum | Tue Oct 05 04:01:36 EDT 1999 | Brian
| Hi, | | Help! Could anyone help to enlighten me on this? | | Question: | | If I have a CSP/BGA package of size X by Y and the standoff gap between the component and PCB is Z, What is the maximum allowable Y/Z or X/Z that using a normal water cl