Electronics Forum | Thu Aug 06 09:23:07 EDT 2009 | karkanov
Hi, I would like to have the pro's and con's about those 2 system: Sony VR-201H and Sony CPC500 and Orbotech advantage S-22 ( and if someone have the spec sheet I'd love to have them too) Thank You
Electronics Forum | Wed Aug 12 04:37:14 EDT 2009 | sachu_70
SAC305 has a liquidous state temperature 217 degC. Check the datasheet to compare to this temp. I suppose, it may be lower. - Cheers !
Electronics Forum | Wed Aug 12 14:37:41 EDT 2009 | davef
Try this: http://www.pwbrc.org/members/pdf/works99/Hua.PDF
Electronics Forum | Fri Aug 21 16:15:09 EDT 2009 | drakealvarez
Define "good price". Throw out a number. Good price - One feeder around $2,000.00 & under if possible would help very much. -Aortiz
Electronics Forum | Thu Aug 20 08:42:32 EDT 2009 | voytek
Do you know if I can use Multi Pitch Tape Feeder from GSM2 platform on GSM and GSM1 platform? Thank you,
Electronics Forum | Thu Aug 20 13:59:42 EDT 2009 | dcell_1t
Hi there! After various trial-error experiments we determined that two factors are the most insignificant in order to reduce or make worst the issue, those factors are: Placement force: regular placement vs "force applied" to dip the component on th
Electronics Forum | Wed Sep 02 11:54:34 EDT 2009 | davef
You can determine empirically what will work. * Use ion chromatography [IPC-TM-650 2.3.28] to evaluate the residues and determine if the residues must be removed. * Use energy dispersive spectroscopy for the elemental analysis or chemical characteriz
Electronics Forum | Tue Sep 01 03:32:53 EDT 2009 | d0min0
Hi BWET we are using a chamber that can take 2 stencils 29 x 29 blowing hot air from one side takes ~30min @ 40 C to dry - but sometimes up to 45mins BR
Electronics Forum | Tue Sep 08 15:00:50 EDT 2009 | thanh
We are looking to buy 1 or 2 Feeder Storage Carts, have any one having extra laying around for sale?? let me know, thanks
Electronics Forum | Wed Sep 16 03:17:47 EDT 2009 | geb
The solder wire uses a ORL0 flux. The wire contains less flux at around 2.0-4.0%.