Electronics Forum | Tue Apr 04 02:23:40 EDT 2023 | josh9476
Hi, I am Josh Jung of the Sales director at Xavis Co., Ltd in S. Korea. We have the several systems for 2D and 3D inline X-ray from 100kV to 180kV. Please send your e-mail to me and I will send you our technical document.
Electronics Forum | Wed Apr 26 19:10:43 EDT 2023 | cyber_wolf
This machines support table looks similar to AP and UP machines. I believe MPM published the dimensions of the "H" tower that the dedicated plates bolts to. As far as the plate, they are typically (2) pieces with the inside hollowed out to allow for
Electronics Forum | Thu May 04 04:29:05 EDT 2023 | abhishek10
we have observed a Field claim in ECU where root cause is Lead lift found in one of the IC. What could be the possible reason for lead lift and how to avoid the same in future. QFP is the Type 1.Checked the Part Library(3-D Check Refernece no.-23
Electronics Forum | Fri Jun 02 06:22:47 EDT 2023 | calebcsmt
We have been using our Pillarhouse Handex Selective for just over a year now. We are finding the nozzles are lasting approx. 3-5 months with w/ SAC305 @ 305C. Generally don't have any issues with wetting and with good maintenance, proper use of th
Electronics Forum | Sun Jun 18 19:59:28 EDT 2023 | smtusa
Seeing this graphic has me rethinking solder paste jetting as alternative to stencil printing. It seems it's only 2-3x faster 80k points per hour vs 28k. Wouldn't it be better to get 10 time pressure dispensers vs 1 solder jet?
Electronics Forum | Fri Jul 07 13:37:46 EDT 2023 | davef
Use the volume of paste of your circular aperture as the starting point. Calculate: Volume = pi X (aperture diameter^2 / 4) X stencil thickness Determine the sides of your square aperture using the volume of paste that you calculated and the stencil
Electronics Forum | Wed Aug 02 06:48:56 EDT 2023 | kirill
Use T5 solder paste Make sure you dont have too much paste, usually 1 time printing instead of 2. Make sure the component is baked before production. Re-check your profile on the reflow. Could be also a bad pcb edit, nothing you can do there.
Electronics Forum | Sun Aug 13 22:31:58 EDT 2023 | cspasol
Hi! I have encountered this problem so many times. Here are the possible cause of your machine problem. 1. PCI board or PCI to motherboard cable. 2. VME memmory card. 3. VME board itself. 4. Power supply for VME board. Hope could help.
Electronics Forum | Tue Aug 22 15:22:46 EDT 2023 | thecolonel97
Our paste manufacturer failed to respond. I did try adding 2 frozen jugs of water into the reservoir tank, this did not lower the cooler 1 temp. We have to have a water or air flow restriction causing this to run hotter. Still currently investigat
Electronics Forum | Mon Oct 02 13:46:53 EDT 2023 | SMTA-72837649
If it's the same as the 32D, 2 things need to happen. Air pressure at the nozzle for atomization, and the solenoid at the bottom of the flux tank needs to open to provide a gravity stream of flux. You should be able to take both hoses off and check f