Electronics Forum | Wed Jun 27 11:13:44 EDT 2012 | mosborne1
We are seeing PLCC socket leads not soldered in our SMT process. We are using a KIC thermal profiling device and we are on 50% greem light process window. All other solder joints on the board looks great. The solder flowed what looks like perfect on
Electronics Forum | Fri Nov 24 11:21:06 EST 2000 | Ramon I Garcia C
HI GUYS: COULD SOMEBODY ELSE SAID ME WHERE TEST THE CONTAMINATION IN BOARDS,NOW I HAVE A PROBLEM WITH SOLDER WAVE PROCESS,THERE ISN�T FLOW ON THRU HOLE. AND I THINK MAYBE IS CONTAMINATION IN PCB. THANKS. RAMON I
Electronics Forum | Wed Aug 30 15:49:25 EDT 2000 | Danny Carr
Luis, Try the Spincircuit web page, they have a om-line component search feature. http://www.spincircuit.com Good luck! Danny Carr
Electronics Forum | Fri May 14 16:11:59 EDT 2004 | pjc
Feeder Systems Unlimited Inc 922 E. Old Willow Rd., Ste. 305 Prospect Heights, 60070 Tel: 1.847.541.8911 SEC Manufacturing Equipment 13313 SW Freeway Suite 248 Sugar Land, Texas, 77478 Tel: (281) 242-1707 Fax: (281) 242-1538
Electronics Forum | Wed Dec 15 09:11:14 EST 2004 | ptavernier
Hi Cardinal, OK. Thank's. It's all right. What do you about SAC305 ? Do we use a linear melting too ?
Electronics Forum | Tue Feb 01 14:33:23 EST 2005 | George
I have been told that If you are not going to do business outside the USA then you don't have to worry about going Lead Free.. Is that correct? Also it seems everyone is leaning towards SAC305. What about SN95/AG4 instead???
Electronics Forum | Fri Feb 04 15:42:34 EST 2005 | Indy
Do a search for SAC305. There will be lots of answers. Jay Brower has done good work on it. Cheers Indy
Electronics Forum | Fri Mar 11 03:53:04 EST 2005 | Rob
1 Euro coin = Centre: Cu75 Ni25 Outer Ring: Cu75 Zn20 Ni5. Think I'd rather go with SAC305. & They don't even have the Queen on!
Electronics Forum | Tue Jun 14 18:32:44 EDT 2005 | GS
Hi Peter, which should be the best cooling rate once belove TAL by using L-F alloy ie. SAC 305 ? Tnks GS
Electronics Forum | Fri Jul 08 09:14:49 EDT 2005 | Jason Fullerton
I've tested boards with SN100C HAL finish, and wetting to the PCB finish was poor at best, using a no clean SAC305 paste.