Electronics Forum | Tue Feb 24 18:04:22 EST 2004 | adlsmt
Im using Hi-Grade 1075 now. Is the 3541 a no-clean?
Electronics Forum | Wed Jul 12 15:29:24 EDT 2000 | Ryan
Does anybody rent reel counters? We just need a couple to finish up inventory count. I can't think of any personally. -Ryan Jennens
Electronics Forum | Mon Feb 23 20:34:14 EST 2004 | greg york
Try Hi-grade Alloy Corp in Chicago we sell the flux over in the Uk and have several companies using 3541 flux on the Versaflow, works really well no bridging or icicling
Electronics Forum | Sat Sep 26 10:40:50 EDT 1998 | Ajit Jain
Can sombody tell, why the boards soldered with no-clean paste be cleaned at all ! I wants to sop cleaning at our plant but technicaljustification is required to convince my customers in Australia & England. Pl. let me know, from where I can find th
Electronics Forum | Mon Jan 14 06:28:18 EST 2008 | gregoryyork
Hi its normally down to the state of cure of the resist type not the actual type be it matt or gloss. If its not cured correctly it will produce solder balls. Pending where you are you could try our 35-41 or new 35-41-30 flux this will reduce the pro
Electronics Forum | Mon Sep 28 12:30:55 EDT 1998 | Bill Schreiber
Remember, even if you are successful in your justification of not cleaning your final product, there will always be a need for cleaning. Screens, stencils, misprinted PCBs, wave solder pallets, squeegees, tooling, etc. New cleaning applications can
Electronics Forum | Sat Sep 26 19:16:54 EDT 1998 | Graham Naisbitt
Ajit, How clean is clean? Are you running fine-line, fine-pitch; COB, BGA, Flip-Chip; making high rel circuits and putting them into a hostile environment? Well, as I have just posted to an earlier similar question on the SMTNet, there is no such thi
Electronics Forum | Mon Feb 23 20:19:15 EST 2004 | greg york
Has anyone ever seen a bulbous joint (on 1 side > of 1 designator) on every board? I checked the > preheat profile at the wave and have played with > dwell times but can't get rid of it. I checked > the archives and didn't find much. Any help wou